采用动电位极化、电化学阻抗和Mort-Schottky等电化学测试方法,研究了在室温、3.5% NaCl溶液条件下,静水压力对纯镍的钝化膜性能的影响.结果表明:随着静水压力的增加,纯镍的腐蚀速度增大,阴极过程保持不变,阳极过程加速.静水压力对阳极过程的影响:一方面提高纯镍钝化膜的抗腐蚀能力,使钝化膜中的受主密度减小,空间电荷层的厚度增加;另一方面,恶化了纯镍的钝化膜腐蚀抗腐蚀能力,使钝化膜变得不稳定,并且表现出较高的化学溶解速度和空穴扩散系数.静水压力对纯镍钝化膜的恶化作用比提高作用对阳极过程的影响更大,导致纯镍的抗腐蚀能力随着静水压力的提高而减小.
参考文献
| [1] | 许立坤,李文军,陈光章.深海腐蚀试验技术[J].海洋科学,2005,29(7):2. |
| [2] | 郭为民,李文军,陈光章.材料深海环境腐蚀试验[J].装备环境工程,2006,3(1):11. |
| [3] | M.Schumcher.Sea Water Corrosion Handbook[M].New Jersey:Noyes Data,1979.107. |
| [4] | E Antoine,L Lemoine,J Peyronnet.Collection of Data on the Cot-rosion of Steels and on the Marine Environment at Great Depth[R].Commission of the European Communities,1982.105. |
| [5] | A M Beecaria,G Poggi.Influence of hydrostatic pressure on pitting of aluminum in sea water.[J]British Corrosion Journal,1985,20(4):183. |
| [6] | A M Becearia,G Poggi,D Gingaud,et al.Effect of hydrostatic pressure on passivating power of corrosion layers formed on 6061 T6 aluminum alloy in sea water[J].British Corrosion Journal,1994,29(1):65. |
| [7] | A M Beccaria,G Poggi.Effect of some surface treatments on ki-netics of aluminum corrosion in NaCI solutions at various hydro-static pressures[J].British Corrosion Journal,1986,21(1):19. |
| [8] | A M Beccaria,P Fiordiponti,G Msttogno.The effect of hydro-static pressure on the corrosion of nickel in slightly alkaline so-ltions containing CIˉions[J].Corrosion Science,1989,29.(4):403. |
| [9] | R Venkatesan.Corrosion of fetrous alloys in deep sea environ-ments[J].British Corrosion Joumal,2002(37):257. |
| [10] | G Goedlet,S Faty,S Cardoso,et al.Influence of nanocrystalliza-tion on passive behavior of Ni-based superalloy in acidic solu-tions[J].Corrosion Science,2004,46:1479. |
| [11] | M Carmezim,A Similes,M Montemor,et al.Semieondueting of passive films formed on Fe-Cr alloys using eapacitiance meas-urements and cyclic voltammerty techniques[J].Corrosion Sci-enee,2005,49:581. |
| [12] | M Belo,N Hakiki,M Ferreira.Semiconducting properties of passive films formed on nickel-base alloys type Alloy 600:influ-once of the alloying elements[J].Electrochimica Acta,1999,44:2473. |
| [13] | M Ferreira,N Hakiki,G Goodlet,et al.Influence of the temper-ature of film formation on the electronic structure of oxide films formed on 304 stainless steel[J].Electrocmhimica Acta,2001,46:3767. |
| [14] | E Sikora,D Maedonald.Nature of the passive film on nickel[J].Electrochimiea Acta,2002,48:69. |
| [15] | E Sikora,J Sikom,D Macdonald.A new method for estimating the diffusivities of vacancies in passive films[J].Electrochimi-ca Acta,1996,41:783. |
| [16] | S Alan,H Kwon.Effects of solution temperature on electronic properties of passive film formed on Fe in pH 8.5 borate buffer solution[J].Electrochimice Acta,2004,49:3347. |
| [17] | N Li,Y Li,S Wang,et al.Effects of nanocrystallization on the corrosion behavior of 309 stainless steel[J].Electrochimiea Ac-ta,2006,52:760. |
| [18] | Y Cheng,C Yang,L Luo.Determination of the diffusivity of point defects in passive films on carbon steel[J].Thin Solid Film,2002,169:416. |
| [19] | H Guo,B Lu,J Luo.Study on passivafion and erosion-enhanced corrosion resistance by Mott-Schottky analysis[J].Electrochim-iea Acta,2006,52:1108. |
| [20] | E Sikora,J Sikora,D Macdonald.Macdonald.A new method for estimating the diffusivities of vacancies in passive films[J].Electrochimiea Acta,1996,41:783. |
| [21] | D Macdonald.Journal of the Electrochemical Society,Journal of the Electrochemical Society,1992,139:3434. |
| [22] | L Liu,Y Li,F Wang.Pitting mechanism on an austenite stain-less steel nanocrystalline coating investigated by electrochemical noise and in-situ AFM analysis[J].Electrechimica Acta,2008,53:2453. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%