用多弧离子镀在镍基高温合金K417G上制备了NiCoCrAlY涂层,对涂层进行了1050℃真空退火4小时、粉末包覆渗铝、1100℃下预氧化1小时等后续预处理;研究了涂层在1000℃下的高温氧化行为.结果表明:真空退火处理使涂层组织更致密,涂层形成β+σ+γ/γ′多相平衡组织,轻微降低了涂层退化倾向;渗铝处理基本消除了涂层内孔洞,降低了表面粗糙度,使涂层表面Al含量大幅增加,形成β相/扩散过渡层/β+σ+γ/γ′三层结构,并延长了涂层的寿命;1100 ℃短时间预氧化使涂层表面形成了α-Al203薄层,阻碍了亚稳态氧化铝膜的形成,从而进一步提高了涂层的抗氧化性能,延迟了涂层退化.

参考文献

[1] 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001.430.
[2] M J Pomeroy.Coatings for gas turbine materials and long term stability issues[J].Materials and Design,2005,26:223.
[3] Shusuo Li,Jinxia Song,Chungen Zhou,et al.Microstrncture evolution of NiCoCrAlY overlay coating for Ni3Al based alloy IC6turbine vane during long term engine test[J].Intermetallics 2005,13 (3-4):309.
[4] Vetter.J,Knotek O,Brand J,et al..MCrAlY Coatings Deposited by Cathodic Vacuum-Arc Evaporation[J].Surface & Coatings Technology,1994,68:27.
[5] B Wang,R F Huang,G H Song,et al.Interdiffusion Behavior of Ni-Cr-Al-Y Coatings Depositd by Arc-Ion Plating[J].Oxidation of Metals,2001,56:1.
[6] Warnes B M.Improved aluminnide / MCrAlX coating systems for super alloys using CVD low activity aluminizing[J].Surface & Coatings Technology,2003,163/164:106.
[7] Achar DRG,Munoz-Arroyo R,Singheiser L,et al.Modelling of phase equilibria in MCrAlY coating systems[J].Surface & Coatings Technology,2004,187:272.
[8] Brossa F,D Dangelo,E Gandini.Structure and Composition of Mcraly Coatings Modified by Al Additions[J].Journal De Physique Iv,1993,3 (C9):559.
[9] T F An,H R Guan,X F Sun,et al.Effect of the θ-α-Al2O3 Transformation in Scales on the Oxidation Behaviors of a Nickel-Base Superalloy with an Aluminide Diffusion Coating[J].Oxidation of Metals,2000,54(3/4):301.
[10] F H Stott.The Oxidation of Alumina-Forming Alloys[J].Materials Science Forum,1997,19:251.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%