主要讨论了电化学方法在材料评估方面的应用原理、方法以及它在实际中的一些成功运用.同时,分析了应用电化学方法在评价材料性能方面进行研究的一些不足和未来的发展方向所在.
参考文献
| [1] | X Mao,W Zhao.Electrochemical Polarization Method to Detect Aging Embrittlement of 321 Stainless Steel[J].Corrosion Engineering,1993,49 (4):335. |
| [2] | Ⅱ-Hyun Kwon,Seung-Se Back,Hyo-Sun Yu.The use of eleetrochemical and mechanical property correlations to monitor the degradation of Cr-Mo-V turbine casing steel[J].International Journal of Pressure Vessels and Piping,2003,80 (3):157. |
| [3] | Shin-ichi Komazaki,Tetsuo Shoji,Iwao Abe,et al.Nondestructive evaluation of creep damage and life prediction of Ni-base superalloy used in advanced gas turbine blades by electrochemical technique[A].Ninth International Symposium on Nondestructive Characterization of Materials[C].Sydney,Australia:AIP,1999.113. |
| [4] | S I Komazak,S Kishi,T Shoji,et al.Creep damage evaluation of W alloyed 9% Cr ferritic steel by electrochemical method[J].材料,2001,50(5):503. |
| [5] | T Shibuy,T Misawa.Electrochemical Evaluation of the Degree of Temper Embrittlement with Modetransfer in Impact fracture Surface of 2.25 Cr-1 Mo Low Alloy Steels[J].材料と環境,1999,48(3):146. |
| [6] | Y Nishiyama,K Fukaya,M Suzuk,et al.Electrochemical Evaluation of Thermal Aging Embrittlement of 2 (1/4) Cr-1MoSteel for a Nuclear Pressure Vessel[A].Small Specimen Test Techniques Applied to Nuclear Reactor Vessel Thermal Annealing and Plant Life Extension(ASTM STP 1204)[C].Philadelphia,USA:ASTM,1993.16. |
| [7] | F Duffaut,J P Pouzet,P Lacombe.Potentiostatic study of structural modifications caused in a Ni-Cr-Fe alloy by heat treatment at 650℃[J].Corrosion Science,1966,6(2):83. |
| [8] | A P Majidi,M A Streicher.Potentiodynamic reactivation method for detecting sensitization in AISI 304 and 304Lstainless steels[J].Corrosion,1984,40 (8):393. |
| [9] | 方智,张玉林,吴荫顺,等.电化学再活化法评价308L不锈钢的晶间腐蚀敏感性[J].腐蚀科学与防护技术,1996,8(2):87. |
| [10] | R F A Jargelius,S Hertaman,E Aymniotis,et al.Evaluation of the EPR technique for Measuring Sensitization in Type 304 Stainless Steel[J].Corrosion,1991,47 (6):429. |
| [11] | H Huang,C Liu,S Chen.Electrolyte System of EPR Test for Detecting Sensitization in Austenitic Stainless Steel[J].Corrosion,1992,48(6):509. |
| [12] | 李广超,杨文忠,路长青,等.可致钝体系中金属阳极腐蚀行为新判据-EPR技术用于测定硫脲对不锈钢阳极腐蚀行为的影响[J].材料保护,2001,34(8):44. |
| [13] | 高中平,陈范才,赵常就.EPR法评价晶间腐蚀敏感性的各种判据的比较[J].中国腐蚀与防护学报,2000,20(4):243. |
| [14] | W L Clarke,R L Cowan,W L Walker.Comparative Methods for Measuring Degree of Sensitization in Stainless Steel[A].Intergranular Corrosion of Stainless Alloys (ASTM STP 656)[C].Philadephia USA:ASTM,1978.99. |
| [15] | N Alonso-Falleiros,M Magri,I G S Falleiros.Intergranuler corrosion in a martensitic stainless steel detected by electrochemical test[J].Corrosion,1999,55(8):769. |
| [16] | S Frangini,A Migrone.Modified electrochemical potentiokinetic reactivation method for detecting sensitization in 12wt% Cr ferritic stainless steels[J].Corrosion,1992,48(9):715. |
| [17] | E Angelini,B De Benedetti,G Maizza,et al.Sensitazation phenomena on aged SAF2205 duplex stainless steel and their control using the electrochemical potentiokinetic reactivation test[J].Corrosion,1999,55(6):606. |
| [18] | G L Edgeman,M Marek,D F Wilson,et al.Sensitization behavior of alloy 800H as characterized by the electrochemical potentiokinetic reactivation (EPR) technique[J].Corrosion,1994,50(12):912. |
| [19] | M Casales,M A Espinoza-Medina.Predicting susceptibility to intergsanular stress corrosion cracking of alloy 690[J].Corrosion,2000,56(11):1133. |
| [20] | S M Bruemmer.Evaluation of chemical and electrochemical etching techniques to determine phosphorus segregation in NiCrMoV rotor steels[J].Corrosion,1986,42 (3):180. |
| [21] | V Cihal,R Stefec.On the development of the electrochemical potentiokinetic method[J].Electrochimica Acta,2001,46:3867. |
| [22] | V Cihal,A Klimaza,S Lasek.Extended Abstract[A].Eurrocorr-96[C].Nice,France:European Corrosion Congress,1996.1. |
| [23] | M L Saucedo-Mumoz,Y Watanabe,T Shoji,et al.An electrochemical study of thermal degradation in austenitic stainless steels[C].Proceedings of Asian Pacific Conference on Fracture and Strength'96,Kyongiu,Korea,June 1996:837. |