钢基身管镀铬层在高温腐蚀性气体中服役,采用YAG激光器对身管内表面作螺旋线状离散淬火预处理后再电镀铬的复合工艺,形成了基体界面呈激光淬火区/激光未处理区周期性变化的铬层/基体结构.对该身管进行高温腐蚀介质为火药气体的靶场实验.对实验后的基体界面腐蚀形貌与铬层剥落的关系研究表明:次界面裂纹的形成是基体界面高温气体腐蚀的根本原因,基体界面腐蚀的结果是形成基体烧蚀坑,烧蚀坑上的铬层以断裂形式剥落.激光淬火预处理钢基体通过抑制次界面裂纹的形成避免了基体界面高温气体腐蚀损伤,提高了铬层的抗剥落能力.
参考文献
| [1] | S Sopok,C Rickard,S Dunn.Thermal-chemical-mechanical gun bore erosion of an advanced artillery system part one:theories and mechanisms[J].Wear,2005,258:659. |
| [2] | S Sopok,C Rickard,S Dunn.Thermal-chemical-mechanical gun bore erosion of an advanced artillery system part two:modeling and predictions[J].Wear,2005,258:671. |
| [3] | P J Cote,Christopher Rickard.Gas-met al reaction products in the erosion of chromium-plated gun bores[J].Wear,2000,241:17. |
| [4] | P J Cote,G Kendall,M E Todaro.Laser pulse heating of gun bore coatings[J].Surface and Coatings Technology,2001,146/147:65. |
| [5] | P J Cote,Sabrina,L Lee,M E Todaro,et al.Application of Laser Pulse Heating to Simulate Thermomechanical Damage at Gun Bore Surfaces[J].Journal of Pressure Vessel Technology,2003,125:335. |
| [6] | PJ Cote,G Kendall,M E Todaro.et al.Gun bore erosion mechanisms revisited with laser pulse heating[J].Surface and Coatings Technology,2003,163/164:478. |
| [7] | J H Underwood,M D Witherell,S Sopok,et al.Thermomechanical modeling of transient thermal damage in cannon bore materials[J].Wear,2004,257:992. |
| [8] | J H Underwood,Edward Troiano.Critical Fracture Processes in Army Cannons:A Review[J].Journal of Pressure Vessel Technology,2003,125:291. |
| [9] | J H Underwood,Anthony P Parker,Gregory N.Vigilante,et al.Thermal Damage,Crackingand Rapid Erosion of Cannon Bore Coatings[J].Journal of Pressure Vessel Technology,2003,125:299. |
| [10] | B Lawton.Thermo-chemical erosion in gun barrels[J].Wear,2001.251:827. |
| [11] | 张喜发,卢兴华.火炮烧蚀内弹道学[M],北京.国防工业出版社.2001.6. |
| [12] | EO CObo,R A Suarez Baldo,J B Bessone.Corrosion of chromium plated rotor in drilling fluid[J].Surface and Coatings Technology,1999,122:39. |
| [13] | 徐永祥,严川伟,高延敏,等.表面状态和处理对涂层下A3钢腐蚀和涂层失效的影响[J].腐蚀科学与防护技术,2003,15(4):208. |
| [14] | 徐永祥,严川伟,高延敏,等.可溶盐污染对涂层下A3钢腐蚀和涂层失效的影响[J].腐蚀科学与防护技术,2003,15(3):137. |
| [15] | 林海潮,李谋成.涂层下金属的腐蚀过程[J].腐蚀科学与防护技术,2002,14(3):180. |
| [16] | 陈光南,罗耕星,张坤.提高镀铬身管寿命的激光强化新方法[J].兵工学报(增刊),2003,12:6. |
| [17] | Huaixue Li,Guangnan Chen,Guoxiang Zhang,et al.Characteristics of the interface of a laser-quenched steel substrate and chromium electroplate[J].Surface & Coatings Technology,2006,201 (3/4):902. |
| [18] | 徐向阳,张坤,陈光南,等.激光硬化基体对镀铬层组织和结合的影响[J].中国激光,2006,33(3):413. |
| [19] | 陈光南,武晓雷,罗耕星,等.管状工件内表面激光强化方法与装置[P].中国.ZL99116728.7. |
| [20] | 曾志银,张军岭.吴兴波.火炮身管强度设计理论[M].北京:国防工业出版社,2001.46. |
| [21] | Pedro De la,Cruz Maguns.Effect of laser hardening on the fatigue strength and fracture of a B-Mn steel[J].Int.J.Fatigue,1998,20(5):389. |
| [22] | M Heitkempar,C Bohne,A Pyzalla,et al.Fatigue and fracture behaviour of a laser surface heat treated martensitic high-nitrogen tool steel[J].Int.J.Fatigue,2003,25:101. |
| [23] | E Altus,E Konstantino.Optimum laser surface treatment of fatigue damaged Ti-6A1-4V alloy[J].Materials Science and Engineering,2001,A302:100. |
| [24] | Yahong Sun,Satoshi Hanaki,Masato Yamashita,et al.Fatigue behavior and fractography of laser-processed hot work tool steel[J].Vacuum,2004,73:655. |
| [25] | 胡国华.材料力学[M].重庆:重庆大学出版社,1992.94. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%