采用X射线衍射(XRD)、扫描电镜(SEM)、X射线电子能谱(EDAX)和金相显微镜(OM)等方法,分析比较了染有"粉状锈"与未染粉状锈的青铜残片的矿物组成、腐蚀层分层结构及金相组织.结果发现,染有"粉状锈"的青铜样品含有未染粉状锈的样品所没有的副氯铜矿;其断面腐蚀层分若干层,且每层锈体的结构和元素组成各不相同,金相分析表明了粉状锈生成属点蚀或晶间腐蚀.