概述了金属在湿H2S环境中的腐蚀破坏类型、腐蚀机理、实验研究方法和影响因素,探讨了湿H2S的定义,提出:在区分溶液H2S和薄液H2S腐蚀的基础上,加强湿H2S环境下腐蚀机理、高温高压湿H2S条件下的腐蚀开裂行为和机理、阳极溶解和HIC的相互关系的研究;发展和规范湿H2S环境下设备腐蚀破坏的检测方法和相关的工业标准,开展H2S环境下寿命预测和安全评估技术工作;完善室内模拟湿H2S环境下腐蚀实验技术.
参考文献
| [1] | 王维宗、贾鹏林、许适群.湿硫化氢环境中腐蚀失效分析[J].石油化工设备技术,2001,22(3):15. |
| [2] | 应道宴.液化石油气球罐的硫化物应力腐蚀破裂[J].腐蚀与防护,1983(2):22. |
| [3] | 于英姿,米秋占,段贵华.输气管道的硫化物应力腐蚀分析[J].油气储运,2000,19(8):37. |
| [4] | 柳曾典.湿硫化氢环境用低合金高强度钢[J].石油化工设备技术,1998,19(5):57. |
| [5] | American Petroleum Institute. Technical Data Book, Phase Equilibrium in System Containing Water[M]. New York: API,1966, 7. |
| [6] | Y M Mu. Applying process modeling to screen refining equipment for wet hydrogen sulfide service[J]. Corrosion, 1998, 54(2): 167. |
| [7] | Canadian Standards Association CSA- Z662 - 94, "Oil and Gas Pipelines[J ]. |
| [8] | European Federation of Corrosion Publication, EFC. A Working Party Report on Guidelines on Material requirements for Carbon and Low Alloy Steels for H2S - Containing Environments in Oil and Gas Production. London, 1995,10. |
| [9] | 王荣贵.化工装置中钢在湿硫化氢环境下的腐蚀机理与设备选材[J].化肥设计,2002,40:5. |
| [10] | ВасиленкоИИ,МелеховРК.著,陈石卿,焦明山译.钢的应力腐蚀开裂[M].北京:国防工业出版社,1983.185. |
| [11] | Tromans D, Ramakrishna S, Hawbolt E B. Stress corrosion cracking of ASTM A516 steel in hot caustic sulfide solutionspotential and weld effects[J]. Corrosion, 1986, 42(2) :63. |
| [12] | Kindlein W, Schilling JR P T, Schroeder R M et al. The characterization of the sulphide stress corrosion susceptibility of high- strength low- alloy steels in standardized solutions[J].Corrosion Science, 1993, 34(8): 1243. |
| [13] | Riecke E M ,Johnen B , Moeller R. The effect of phosphorus on hydrogen uptake by iron in acidic suplphate and sulphide solutions[J]. Corrosion Science, 1987, 27(10) : 1027 |
| [14] | Greer J B. Factors affecting the sulfide stress cracking performance of high strength steels [J]. Materials performance,1975, 14(3): 11. |
| [15] | 褚武扬,肖纪美,李世琼.钢中氢致开裂机理[J].金属学报,1981,17:10. |
| [16] | Li J C M. Computer simulation of dislocations emitted from a crack[J]. Scripta Metal., 1986, 20:1477. |
| [17] | Lu H, Li M D, Zhang T C, et al. Hydrogen - enhanced dislocation emission, motion and nucleation of hydrogen - induced cracking for steel[J ]. Science in China, 1997, 40:530. |
| [18] | 褚武扬,乔利杰,陈奇志,等.断裂与环境断裂[M].北京:科学出版社,2000:221. |
| [19] | H Huang and W J D Shaw. Cold work effects on sulfide stress cracking of pipeline steel exposed to sour environments [J].Corrosion Science, 1993, 34 ( 1 ): 61. |
| [20] | 左禹、张树霞.1Cr18Ni9Ti不锈钢在硫化氢水溶液中的台阶状应力腐蚀破裂[J].北京化工学院学报,1994,21(4):58. |
| [21] | 郑华均,张康达,董绍平.16MnR钢在不同饱和硫化氢溶液应力腐蚀的试验研究[J].压力容器,1991(1):4. |
| [22] | W Chen, F King, EVokes. Characteristics of near - neutral pH stress corrosion cracks in an X- 65 pipeline[J]. Corrosion,2002, 58(3) :267. |
| [23] | Tsai S Y, Shih H C. A statistical failure distribution and lifetime assessment of the HSLA steel plates in H2S containing enviromments[ J ]. Corrosion science, 1996, 38(5), 705. |
| [24] | 小若正伦(日).金属的腐蚀破坏与防蚀技术[J].北京:化学工业出版社,1988:112. |
| [25] | 王晓燕.CF-62钢在硫化氢环境中的电化学行为和应力腐蚀研究[D].上海:华东理工大学博士学位论文,2001.8. |
| [26] | Kawashima A, Hashimoto K, Shimodaira S. Hydrogen electrode reaction and hydrogen embrittlement of mild steel in hydrogen sulfide solutions[J]. Corrosion, 1976, 32(8) :321. |
| [27] | Houyi Ma, Xiaoliang Cheng, Guiqiu Li et al. The influence of hydrogen sulfide on corrosion of iron uner different conditions [J]. Corrosion Science, 2000, 42:1669. |
| [28] | K Videm, J Kvarekval. Corrosion of carbon steel in carbon dioxide- saturated solutions containing small amounts of hydrogen sulfide[J]. Corrosion, 1995, 51(4) :260. |
| [29] | 吕明,韩薇,付超,等.管线钢焊缝区硫化物应力腐蚀裂开与硫化氢浓度的关系[J].全面腐蚀控制,1990,4(4):8. |
| [30] | 谭志文,杜元龙,陆征,等.硫化物应力腐蚀裂列时硫化氢极限浓度的研究[J].材料保护,1987,20(5):9. |
| [31] | Staehle R W, Fortv A J, Roovan D ED. Fundamental aspects of stress corrosion cracking, NACE, Houston, 1969. |
| [32] | 彭建雄,刘烈炜,胡倩.碳钢在CO2-H2S体系中的腐蚀规律研究[J].腐蚀与防护,2000,21(2):60. |
| [33] | 阎丽静,林海潮,吴维雯.含H2S的硫酸溶液中Cl-对铁阳极溶解的影响[J].中国腐蚀与防护学报,1999,19(2):79. |
| [34] | 阎丽静,牛林,林海潮等.含H2S的硫酸溶中Cl-对铁阳极溶解的影响[J].中国腐蚀与防护学报,1999,19(4):214. |
| [35] | 杨怀玉,陈家坚,曹楚南等.H2S水溶液中的腐蚀与缓蚀作用机理的研究V咪唑啉衍生物在H2S溶液中的缓蚀作用特征[J].中国腐蚀与防护学报,2001,21(6):321. |
| [36] | 王慧龙、刘宏芳、郑家燊.缓蚀剂在HCl-H2S盐水体系中对碳钢的缓蚀作用[J].材料保护,2002,35(1):15. |
| [37] | 郑文龙、于青.钢的环境敏感断裂[M].北京:化学工业出版社,1988:97. |
| [38] | Li J C M. Computer simulation of dislocations emitted from a crack[J]. Scripta Metal., 1986, 20(11): 1477. |
| [39] | 蒲海山,王洪刚.热处理和金相组织对抗H2S应力腐蚀钻材、输油气管用钢性能的影响[J].金属热处理,1998(4):3. |
| [40] | Liao C M, Lee J L. Effect of molybdenum on sulfide stress cracking resistance on low - alloy steels[J]. Corrosion, 1994,50(9), 695. |
| [41] | Liou H Y, Shieh R I, Wei F I, et al[J]. Corrosion, 1993, 49(5):389. |
| [42] | 张学元,杜元龙,郑立群.16Mn钢在H2S溶液中脆断敏感性[J].材料保护,1998,31(1):3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%