介绍了在不同性质应力(拉应力或压应力)作用下氧化膜开裂和剥落的方式和特点及发生开裂和剥落的临界温度变化条件.简述了在外加应力作用下氧化膜的破裂行为及改善氧化膜力学完整性的主要方法.
参考文献
| [1] | Hales R, Smith A F, Killeen J C. Proc. BNES Conf. On Corros. of Steels in CO2, 1974 (Reading), 311 |
| [2] | Evans H E, Hilton D A, Holm R A. Oxid. Metals, 1976, 10:149 |
| [3] | Bastow B D, Whittle D P, Wood G C. Oxid. Metals, 1978,12:413 |
| [4] | Evans H E, Hilton D A, Holm R A, et al. Oxid. Metals, 1980,14:235 |
| [5] | Schutze M. Mater. Sci Tech., 1988, 4:407 |
| [6] | Stott F H. Mater. Sci. Tech., 1988, 4: 431 |
| [7] | Jedlinski J, Bennet M J, Evans H E. Mater. at High Temp.,1994, 12:169 |
| [8] | Evans H E, Lobb R C. Corros. Sci., 1984, 24: 209 |
| [9] | Evans H E, Lobb R C. Ninth International congress on Metallic Corrosion, BRC. Ottawa, 1984 |
| [10] | Asher J, Sugden S, Bennett M J, et al. Werkst. Korros., 1987,38: 506 |
| [11] | Crouch A G, Dooley R B. Corros. Sci., 1976, 16:341 |
| [12] | Hancock P, Hurst R C. Adv. Corros. Sci. Technol., 1974, 4:1 |
| [13] | Tylecote R F. J, Iron Steel Inst. London, 1960,196:135 |
| [14] | Armitt J, Holmes D R, Manning M I, et al. The Spalling of Steam Grown Oxide from Superheater and Reheater Tube Steels, EPRI Rep. FP - 585, 1978 |
| [15] | Grosskreutz J C.J. Electrochem. Soc., 1969, 116:1232 |
| [16] | Hancock R, Nicholls J R. Mater. Sci. Technol., 1988, 4: 398 |
| [17] | Tien J K, Davidson J M. in J V Cathcart(ed. ), Stress Effects on the Oxidation of Metals, AIMB, Warrendalw, PA, 1974.200 |
| [18] | Evans H E. Mater. Sci. Technol., 1988, 4:1079 |
| [19] | Bdrchtold L, Welker M, Sockel H G. Werkst. Korros., 1986,37:145 |
| [20] | Barbehon J, Rahmel A, Schutze M. Oxid. Met., 1988, 28: 85 |
| [21] | Evans U R. An Introduction to Metallic Corrosion, Edward Arnold, London, 1948:194 |
| [22] | Hutchinson J W, Suo Z. advances in Applied Mech., 1991, 29:63 |
| [23] | Tetelman A S, Mcevily A J. Jr. Fracture of Structral materials, John Wiley, New York, 1957, chap. 2 |
| [24] | Manning M I , Metcalfe E. Sixth European Congress on Metallic Corrosion, London, 1977.121 |
| [25] | Evans H E. Mater. Sci. Teehnol., 1988, 4:415 |
| [26] | Evans H E. Corros. Science, 1983, 23:495 |
| [27] | Noden J D, Knights C J, Thomas M W. Br. Corros. J., 1968,3:49 |
| [28] | Wells C H, Follansbee P S, Dils R R. Stress Effects and the Oxidation of Metals (ed. Cathcart J V), AIME, New York,1975. 220 |
| [29] | Schutze M. Mater. Sci. Tech., 1990, 6: 32 |
| [30] | Schutze M. Oxid. Met., 1986, 25:409 |
| [31] | Robertson J, Manning M I. Mater. Sci. Tech., 1990, 6: 81 |
| [32] | Berchtold L, Sockel H G, Ilschner B. in behaviour of high temperature alloys in aggressive environments', (ed. I. Dirman et al.), London, The Metals Society, 1980: 927 |
| [33] | Berchtold L, Welder M, Sockel H G. Werkst. Korrro., 1986,37:145 |
| [34] | Manning M I. in ' Corrosion and mechanical stress at high temperatures', (ed. B. Guttmann and M. Merz), London, Applied Science, 1980. 323 |
| [35] | Riedel H. Met. Sci., 1982, 16:569 |
| [36] | Whittle D P, Stringer J. Proc. R. Soc., 1980, A295:309 |
| [37] | Bennett M J, Moon D P. Proc. Conf. on ' the reactive element effect', (cc. E. Lang), Amsterdam, Elsevier, 1989. |
| [38] | Pendse R , Stringer J. Oxid. Met., 1985,23:1 |
| [39] | Lees D J. Oxid. Met., 1987, 27:75 |
| [40] | Smeggil J, Funkenbusch A W, Bomstein N S. Metall. Trans.,1986, 17A: 923 |
| [41] | Smialek J L. Metall. Trans., 1987, 18A: 164 |
| [42] | Briant C L, Luthra K L. Metall. Trans., 1988, 19A: 2099 |
| [43] | Nicholis J R, Hancock P. In ' the reactive element effect' (ed.E. Lang), Amsterdam, Elsevier, 1989. |
| [44] | Evans A G, Hutchinson J W. Acta Metall., 1989, 37: 909 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%