综述了近年来国内外热浸Zn-Ni合金镀层技术(Technigalva)的研究及生产应用现状.与常规热饺Zn层相比，在Zn浴中加入约0.04～0.09％的Ni获得的镀层厚度适宜，外观更光亮、平滑，并有较好的耐蚀性和粘附性.
参考文献
| [1] | Sandelin R W. Wire and Wire Products, 1940,15:655 |
| [2] | Chen Z W, Kennon N F, See J B, et al. J. of Metals, 1992, 44(1):22 |
| [3] | Lu Jintang, Chen Jinhong, Xu Qiaoyu. Proc. 2nd Asian-Pacific General Galva. Conf., JGS, Kobe, 1994. 287 |
| [4] | Stroud D. Proc. 1st Asian - Pacific General Galva. Corf.,Taibei, 1992.169 |
| [5] | Richard F.J.of Metals, 1987, 39(8) :39 |
| [6] | Bousquet A. Report on General Assembly of European General Galvanizers Association. Eire (June 1987) , ZDA, 1987.2.4 |
| [7] | Skenazi A F, Rollez D. Proc. 15th Inter. Conf. on Hot dip Galva., Rome(1988), ZDA, 1988. CE2 |
| [8] | Allen C J, Kolisnyk P S. Proc. 2nd Asian - Pacific General Galva. Conf. ,JGS, Kobe, 1994.269 |
| [9] | 卢锦堂,陈锦虹,许乔瑜等.材料保护,1995,28(3)：9 |
| [10] | Sven Belfrage, Peter Ostrom. Proc. 15th Inter. Corf. on Hot dip Galva., Rome(1988), ZDA, 1988. CE3 |
| [11] | Notowidjojo B D, Kennon N F, Wingrovo A L. AIMF, 1989.623 |
| [12] | Foct J, Reumont G, Dauphin J Y, et al. Proc. Inter. Conf. on Zinc and Zinc Alloy coated steel sheet, Tokyo, 1989.443 |
| [13] | Habraken L. Proc. 12th Inter. Conf. On Hot Dip Galva. ,Paris (1979), ZDA, 1981.121 |
| [14] | 卢锦堂,陈锦虹,许乔瑜等.材料保护,1996,29(9)：11 |
| [15] | Sokolowaki R, Vieille - Montagne. Proc. 15th Inter. Conf. on Hot dip Galva., Rome(1988), ZDA, 1988. CE1/3 |
| [16] | 卢锦堂,陈锦虹,许乔瑜等.华南理工大学学报,1997,25(8)：48 |
| [17] | 罔襄二,朝野秀次朗等.铁と銅,1982,68：A57 |
| [18] | Beckers S. Report on General Assembly of European General Galvanizers Association. Dublin, Eire, ZDA, 1987.2.1 |
| [19] | Discussion Session E: Proc. 15th Inter. Conf. on Hot dip Galva., Rome(1988), ZDA, 1988. CE1 |
| [20] | See J B. Proc. 2nd Asian - Pacific General Galva. Conf,Kobe, JGS, 1994.58 |
| [21] | Mackowiak J, Short N R. Inter. Metals Reviews, 1979, 1:1 |
| [22] | 陈锦虹,卢锦堂,许乔瑜等.华南理工大学学报,1996,24(2)：43 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%