采用金相(OM)、俄歇(AES)、扫描电镜(SEM)及透射电镜(TEM)等技术手段对实海暴露试样进行探测分析,揭示了表面膜缺陷(如碳膜)、晶界缺陷(晶界析出物)等加速该合金腐蚀进程的试验现象和内在根据,特别指出影响该合金海水腐蚀产物膜稳定性的主要因素,分析了其中的沿晶扩散及应变诱生调幅分解与沿晶腐蚀、沿晶脆断的相互关系.
参考文献
| [1] | Syrett B C, Wing S S. Corrosion/NACE, 1980,36(2): 73 |
| [2] | Syrett B C. Corrosion/NACE, 1976,32(6):242 |
| [3] | Efird K D. Material Performance, 1976,Apr. 16 |
| [4] | Efird K D. Corrosion/NACE, 1977,33(10):347 |
| [5] | Schrader M E. Appl. Surf. Sci., 1982,10(3): 431 |
| [6] | Richter F, Pepperhoff W. Z. Metallk, 1987,74(8): 500 |
| [7] | Lennox T J. Groover R E, Peterson M H. Material Performance, 1971, 10(7):31 |
| [8] | Ijsseling F P, Drolenga L P, Kolster B H. Br. Corrosion J., 1982,17(4):162 |
| [9] | Macdonald D D, Syrett B C, Wing S S. Corrosion/NACE, 1978,34(9): 289 |
| [10] | Syrett B C, Macdonald D D, Wing S S. Corrosion/NACE, 1979,35(9): 409 |
| [11] | Glover T J. Br. Corrosion J., 1982,17(4): 155 |
| [12] | Marsder D D. Material Performance, 1978,17(8): 9 |
| [13] | Todhunter H A. Corrosion, 1960,16(5): 266 |
| [14] | Lopez H V M, Sano N, Sakura T, et al. Acta. Metall. Mater., 1993,41(1): 265 |
| [15] | Bennett L H, Swartzendruber L J. Acta Metall., 1970, 18(5): 485 |
| [16] | Drolenga L J P, Ijsseling F P, Koster B H. Werkst. Korros., 1983,334(4):167 |
| [17] | Sridhar N, Cragnolino G A. Corrosion, 1993,49(12): 967 |
| [18] | Beccaria A M, Crousier J. Br. Corrosion J., 1991,26(3): 215 |
| [19] | 林乐耘,刘少峰,朱小龙.中国腐蚀与防护学报,1997,17(1):1 |
| [20] | 刘少峰,林乐耘.材料研究学报,1997,12(1):20 |
| [21] | 林乐耘,王晓华,严宇民.稀有金属,17(4):275 |
| [22] | Efird K D. Corrosion, 1975,31(3): 275 |
| [23] | 林乐耘,罗德清.腐蚀科学与防护技术,1990,2(2):16 |
| [24] | Guire G E Mc. J. Electrchem. Soc., 1978,125(11):1801 |
| [25] | 朱小龙,林乐耘,雷廷权.金属学报, 1997 ,33(12):1256 |
| [26] | 马兹*希拉特著,赖和怡译.合金扩散和热力学,北京: 冶金工业出版社, 1986, 6.2 |
| [27] | 刘玉清,刘锦岩著.高温合金晶界间隙相,北京: 冶金工业出版社,1990 |
| [28] | Khachaturyan A G, Theory of Structural Transfor. in Solids, John Wiley and Sons,1983 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%