利用差热分析仪对环氧树脂 E51/聚酰胺650体系的固化反应过程进行测试.分析了固化剂添加量、改性剂种类及粉煤灰微珠对体系固化反应的影响.结果表明,固化促进剂和粉煤灰微珠会降低反应起始温度,促进反应进行；固化剂添加量和稀释剂等对固化温度影响较小.根据实验结果确定预固化温度为80℃,制备固化试样并进行 DTA 测试,由测试结果确定后固化温度为120℃.结合预固化温度和后固化温度制备不同的固化试样测试其红外谱线,并利用内标法计算环氧基面积表征固化度,最终确定最优固化制度为预固化温度80℃(120 min),后固化温度120℃(30 min).
The DTA method was used to investigate the curing process of epoxy resin and polyamide system. Effects of the amount of curing agent/ type of modifiers/cenosphere were studied.The result showed that cu-ring promoter and cenosphere can promote the reaction and make the reaction temperature lower than before. The amount of curing agent and diluents have little effect on reaction temperature.According to the experimen-tal results,we determine the pre-curing temperature was 80 ℃ and preparing the sample.Testing the curing sample and then decide the post-curing temperature was 120 ℃.Analysis the specimens made by different cu-ring system by FT-IR and calculating the area of epoxy peak by internal standard method,determined the opti-mal curing system was pre-cured at 80 ℃(120 min),post-cured at 120 ℃(30 min).
参考文献
| [1] | 郭金龙,郭文瑛,谢汝剑,李远明,杨医博.环氧砂浆固化剂的研究进展[J].功能材料,2010(z1):20-22. |
| [2] | Thomas C;Borges P H R;Panzera T H et al.Epoxy composites containing CFRP powder wastes[J].Compos-ites Part B:Engineering,2014,59:260-268. |
| [3] | 吴唯,刘明昌,陈玉,浦伟光,吴祥.E-51环氧树脂固化反应中动力学转变[J].复合材料学报,2011(04):1-6. |
| [4] | 梁玮,李镇江,张林.纳米SiO2/聚氨酯/环氧树脂复合体系的合成及表征[J].功能材料,2013(07):922-925,931. |
| [5] | 刘美华,李程,刘志勇.活性稀释剂环氧环己烷对聚酰胺-胺固化环氧树脂体系性能的影响[J].中南大学学报（自然科学版）,2013(02):520-525. |
| [6] | 林益军,朱祖钊,全春生,姚宪法,金日光.固化促进剂对环氧树脂固化物性能的影响[J].热固性树脂,2011(04):22-25. |
| [7] | Srivastava V K S .Tensile and fracture properties of epoxy resin filled with flyash particles[J].Journal of Materials Science,1990,25(08):3513-3516. |
| [8] | Jian Gu;Gaohui Wu;Qiang Zhang .Preparation and damping properties of fly ash filled epoxy composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):614-618. |
| [9] | 李文秀,张兵,陈立峰,张冰,张志刚.KH-570修饰的SiO_2膜制备及CH_4/CO_2的分离[J].功能材料,2012(05):638-641. |
| [10] | Zhao Jinqqiu;Wang Shanqi.A study on curing charac-teristics of epoxy resin as matrix for frp with infrared spectrum method[J].Acta Materiae Compositae Sinica,1989(01):26-31. |
| [11] | Wan Yong;Lin Shengling .Stude on preparation and properties of MMT/epoxy[J].Journal of Functional Ma-terials,2011,42(z3):442-445. |
| [12] | 甘厚磊,易长海,吕鹏举,陈洁,徐卫林.MOCA/环氧树脂体系的固化行为[J].高分子材料科学与工程,2009(02):119-122. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%