以二乙醇胺(DEA)和丁二酸酐为原料,甲醇为溶剂,合成一种新型羧酸型亲水单体 N,N-二羟乙基-2-氨基丙酸(DMCA),优化得到 DMCA 的最佳条件为：冰水浴0℃,n (DEA)∶n (丁二酸酐)为1∶1．2,时间为80 min,甲醇用量为300 mL/mol(DEA),在最佳条件下 DMCA 的转化率为86．18％.采用红外(FT-IR)、核磁(1 H NMR)、X 射线衍射(XRD)、热重(TG)、元素分析等手段对 DMCA 进行结构和性能的表征.以 DMCA 作为亲水扩链剂制备超支化水性聚氨酯 DMCA-HWPU,其性能检测结果表明,DMCA-HWPU 为非结晶性体系,其乳液呈乳白色泛蓝光,无沉淀,乳液稳定性高,并且具有很好的热稳定性.
With diethanolamine (DEA)and succinic anhydride as raw materials and methanol alcohol as solvent, a new carboxylic acid type of hydrophilic monomer DMCA was synthesized.The best conditions for synthetic hydrophilic monomer were:temperature 0 ℃,mole ratio 1∶1.2,time 80 min,solvent dosage was 300 mL/mol (DEA).Under the best conditions,the conversion rate had reached 86.18%.The structure and performance was charaterized by FT-IR,1 H NMR,XRD,TG and element analysis.Hyperbranched waterborne polyurethane DMCA-HWPU was synthesized by using DMCA as hydrophilic chain extender.Performance test results showed that:DMCA-HWPU system is non-crystalline,the emulsion is milky and blue light without precipitation,has high emulsion stability and good thermal stability.
参考文献
| [1] | 张发兴,卫晓利.亲水扩链剂对水性聚氨酯性能的影响[J].胶体与聚合物,2008(04):21-23. |
| [2] | Song Wensheng;Xu Cuicui;Zhang Lin.Preparation method and properties of sulfonic acid waterborne polyu-rethane dispersion[A].,2010:338-343. |
| [3] | Lee DK;Tsai HB;Wang HH;Tsai RS .Aqueous polyurethane dispersions derived from polycarbonatediols[J].Journal of Applied Polymer Science,2004(4):1723-1729. |
| [4] | Vanesa Garcia-Pacios;Yoshiro Iwata;Manuel Colera .Influence of the solids content on the properties of waterborne polyurethane dispersions obtained with polycarbonate of hexanediol[J].International Journal of Adhesion & Adhesives,2011(8):787-794. |
| [5] | M.Angeles Perez-Liminana;Francisca Aran-Ais;Ana M.Torro-Palau;A.Cesar Orgiles-Barcelo;Jose Miguel Martin-Martinez .Characterization of waterborne polyurethane adhesives containing different amounts of ionic groups[J].International Journal of Adhesion & Adhesives,2005(6):507-517. |
| [6] | Li Shaoxiong;Zhu Lumin.Polyurethane[M].Jiangsu Sci-ence and Technology Press,1992:552. |
| [7] | Chao Kun;Wu Jianfen;Sun Jianzhong et al.[J].Poly-mer Bulletin,1994,3:156-161. |
| [8] | 王学川,任静,强涛涛.水性聚氨酯亲水性扩链剂的研究进展[J].化工进展,2014(02):432-438. |
| [9] | Zhou Haifeng;Xiong Qiansheng;Xu Gewen.Research on sulfonate waterborne polyurethane[A].,2008 |
| [10] | Li Shaoxiong;Liu Yijun.Polyurethane resin and applica-tion thereof[M].北京:化学工业出版社,2002:161-122. |
| [11] | 王学川,伏芋桥,任龙芳,强涛涛,任静.聚四氢呋喃醚二醇脂肪族超支化聚氨酯的合成及表征[J].功能材料,2013(02):289-293. |
| [12] | Wu H;Xu J;Liu Y et al.Hyperbranched aliphatic poly-ester grafted attapulgite via a melt polycondensation process[J].Journal of Applied Polymer Science,1999,72:151-163. |
| [13] | Louis Boogh;Bo Pettersson;Jan-Anders E. Manson .Dendritic hyperbranched polymers as tougheners for epoxy resins[J].Polymer: The International Journal for the Science and Technology of Polymers,1999(9):2249-2261. |
| [14] | Raffaele Mezzenga;Louis Boogh;Jan-Anders E. Manson .A review of dendritic hyperbranched polymer as modifiers in epoxy composites[J].Composites science and technology,2001(5):787-795. |
| [15] | Mancyzk K;Szewczyk P .Highly branched high solids al-kyd resins[J].Progress in organic Coatings,2002,44:99-109. |
| [16] | Zhu SW.;Shi WF. .Flame retardant mechanism of hyperbranched polyurethane acrylates used for UV curable flame retardant coatings[J].Polymer Degradation and Stability,2002(3):543-547. |
| [17] | Johansson M;Malmstrom E;Jansson A et al.Synthesis and characterization of hyperbranched polyurethane-urea coatings[J].Coat Technol,2000,72:49-58. |
| [18] | 王黎,唐进伟,童身毅.超支化聚氨酯水分散体的合成及其涂膜性能[J].现代涂料与涂装,2007(04):14-16. |
| [19] | Jena KK;Chattopadhyay DK;Raju KVSN .Synthesis and characterization of hyperbranched polyurethane-urea coatings[J].European Polymer Journal,2007(5):1825-1837. |
| [20] | Choi JY;Tan LS;Baek JB .Self-controlled synthesis of hyperbranched poly(ether ketone)s from A(3)+B-2 approach via different solubilities of monomers in the reaction medium[J].Macromolecules,2006(26):9057-9063. |
| [21] | 刘检仔,潘肇琦,杲云.硬段含量对嵌段聚脲结构与性能的影响[J].华东理工大学学报（自然科学版）,2006(10):1187-1191. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%