通过控制金属草酸盐前驱体的热分解过程，用一步法合成了不同n(Fe)/n(Co)的铁钴尖晶石型介孔氧化物。利用XRD、TEM、BET 及振动样品磁强计等研究手段对样品的结构、性能进行了表征。实验表明，所制得的样品具有良好的介孔结构及磁性能。随着n(Fe)/n(Co)的升高，样品的比表面积和最可几孔径增大，饱和磁化强度增加。随着烧结温度增加，饱和磁化强度增加，比表面积降低。
Mes-structured Fe-Co oxides with different Fe/Co molar ratios have been successfully fabricated through one-step pyrolytic method using homogeneous complex oxalates as precursors.The prepared samples were characterized by X-ray diffraction (XRD),transmission electron microscopy (TEM),N2 adsorption/de-sorption and vibrating sample magnetometer techniques.It is shown that the prepared samples possessed homo-geneous mesopores and good magnetic properties.With the increase of Fe-Co molar ratios,the specific areas, the pore size at the maximum probability and the specific saturation magnetization (Ms )increased.In addition, the specific saturation magnetization (Ms )still increased but the specific areas decreased with calcining tempera-ture increasing.
参考文献
| [1] | Yuqiu Qu;Haibin Yang;Nan Yang .The effect of reaction temperature on the particle size, structure and magnetic properties of coprecipitated CoFe_2O_4 nanoparticles[J].Materials Letters,2006(29/30):3548-3552. |
| [2] | Deng Longjiang;Xie Jianliang;Liang Difei et al.The de-velopment and application of magnetic materials in the field of RAM[J].Journal of Functional Materials,1999,30(02):3. |
| [3] | Lixia Wang;Jianchen Li;Yingqi Wang.Adsorption capability for Congo red on nanocrystalline MFe2O4 (M = Mn, Fe, Co, Ni) spinel ferrites[J].Chemical engineering journal,2012:72-79. |
| [4] | Ajroudi L;Villain S;Madigou V et al.Synthesis and microstructure of cobalt ferrite nanoparticles[J].Journal of Crystal Growth,2010,312:2465-2471. |
| [5] | Andre Luis Lopes-Moriyama;Veronique Madigou;Carlson Pereira de Souza.Controlled synthesis of CoFe2O4 nano-octahedra[J].Powder Technology: An International Journal on the Science and Technology of Wet and Dry Particulate Systems,2014:482-489. |
| [6] | Maaz K;Mumtaz A;Hasanain SK;Ceylan A .Synthesis and magnetic properties of cobalt ferrite (CoFe2O4) nanoparticles prepared by wet chemical route[J].Journal of Magnetism and Magnetic Materials,2007(1):289-295. |
| [7] | Yanyan Sun;Guangbin Ji;Mingbo Zheng .Synthesis and magnetic properties of crystalline mesoporous CoFe2O4 with large specific surface area[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2010(5):945-952. |
| [8] | Stefanie Haffer;Till Walther;Roberto Koferstein .Nanostructure-Related Magnetic Properties of Various Mesoporous Cobalt Oxide and Cobalt Ferrite Spinel Phases[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2013(46):24471-24478. |
| [9] | Zhu Shu;Yu Chen;Weimin Huang.Room-temperature catalytic removal of low-concentration NO over mesoporous Fe-Mn binary oxide synthesized using a template-free approach[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2013:42-50. |
| [10] | M. Abdus Salam;Suriati Sufian;T. Murugesan .Catalytic hydrogen adsorption of nano-crystalline hydrotalcite derived mixed oxides[J].Chemical Engineering Research & Design: Transactions of the Institution of Chemical Engineers,2013(12):2639-2647. |
| [11] | Abolfazl Biabani-Ravandi;Mehran Rezaei.Low temperature CO oxidation over Fe-Co mixed oxide nanocatalysts[J].Chemical engineering journal,2012:141-146. |
| [12] | Cao Jianliang;Li Gaojie;Wang Yan et al.Mesoporous Co-Fe-O nanocatalysts:Preparation,characterization and catalytic carbon monoxideoxidation[J].Journal of Environmental Chemical Engineering,2014,2:477-483. |
| [13] | 杨华明,张花,欧阳静,李咸伟,王淀佐.介孔材料分形表征的研究进展[J].功能材料,2005(04):495-498,502. |
| [14] | Li Gengnan;Li Liang;Shi Jingjing et al.One-pot pyrolyt-ic synthesis of mesoporous MCo2 O4(4.5)(M=Mn,Ni, Fe,Cu)spinels and its high efficient catalytic properties for CO oxidation at low temperature[J].Journal of Mo-lecular Catalysis A:Chemical,2014,390:97-104. |
| [15] | Gong Yuanxun;Zhen Liang;Shao Wenzhu et al.Hydro-thermal synthesis and high frequency electromagnetic properties of CoFe2 O4 particles with different scale[J].Journal of Functional Materials,2007,3:1039-1041. |
| [16] | Sato Turtelli R;Duong G V;Nunes W et al.Magnetic properties of nanocrystalline CoFe2 O4 synthesized by modified citrate-gel method[J].Journal of Magnetism and Magnetic Materials,2008,320:e339-e342. |
| [17] | Biabani-Ravandi, A.;Rezaei, M.;Fattah, Z..Low-temperature CO oxidation over nanosized Fe-Co mixed oxide catalysts: Effect of calcination temperature and operational conditions[J].Chemical Engineering Science,2013:237-244. |
| [18] | LF.F.P.G. Braganca;M. Ojeda;J.L.G. Fierro.Bimetallic Co-Fe nanocrystals deposited on SBA-15 and HMS mesoporous silicas as catalysts for Fischer-Tropsch synthesis[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2012:146-153. |
| [19] | Liu Peisheng;Huang Linguo .Preparation metnods for porous metal materials[J].Journal of Functional Materi-als,2002,33(01):5-8. |
| [20] | Sing K S W;Everett D H;Haul R A W et al.Reporting physisorption data for gas/solid systems with special ref-erence to the determination of surface area and porosity[J].Pure and Applied Chemistry,1985,57(04):603-619. |
| [21] | Najmeh Najmoddin;Ali Beitollahi;Eamonn Devlin.Magnetic properties of crystalline mesoporous Zn-substituted copper ferrite synthesized under nanoconfinement in silica matrix[J].Microporous and mesoporous materials: The offical journal of the International Zeolite Association,2014:346-355. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%