采用乙二醇作为溶剂,硫代乙酰胺作为硫源,通过微波液相合成法制备出颗粒大小均一的Cu2 ZnSnS4(CZTS )纳米颗粒.采用 XRD、Raman、EDS、TEM以及 UV-Vis-Nir 等表征手段对所制备的纳米颗粒的物相、元素比例、形貌以及光学性能进行了分析.测试结果表明,所制备的 CZTS 纳米颗粒为(112)择优取向的锌黄锡矿结构,纳米颗粒的平均尺寸约为3．4 nm,其光学带隙为1．85 eV,呈现出明显的量子尺寸效应导致的光学带隙蓝移现象.将 CZTS纳米颗粒制成CZTS墨水并滴涂烘干形成了 CZTS 薄膜,其XRD和SEM结果表明,所制备的 CZTS 薄膜具有良好的结晶性,且表面较为致密.光照与暗态的 I-V曲线测试表明,所制备薄膜具有明显的光电导效应.
In this paper,Cu2 ZnSnS4 (CZTS)nanoparticles were synthesized with ethylene glycol as solvent and thioacetamide as sulfur source by microwave irradiation assisted solvothermal method.The structure,shape, composition and optical properties of as-synthesized CZTS nanoparticles were investigated with X-ray diffrac-tion,Raman spectroscopy,scanning electron microscopy,energy dispersive spectrometer and UV-Vis-Nir spec-troscopy.The results show that the as-synthesized nanoparticles have kesterite structure and stoichiometric composition.The average size of the CZTS nanoparticles was about 3.4 nm.And the band gap of CZTS nanopar-ticles was 1.85 eV,which shows an apparent band gap blue-shift due to the quantum size effect.CZTS ink was formed from CZTS nanoparticles and then CZTS thin films were on glass substrates by drop casting (ink-print method).The results of XRD and SEM from the CZTS thin films show the as-prepared CZTS thin film has a good crystalline and the surface is compact.The CZTS thin film has an obvious photoconductive effect by I-V test under light illumination and darkness.
参考文献
| [1] | 闫勇,张艳霞,李莎莎,晏传鹏,刘连,张勇,赵勇,余洲.非晶CIGS前驱膜无硒退火的相变历程[J].功能材料,2012(21):2902-2905,2911. |
| [2] | 张冷,张维佳,宋登元,张辉,张雷,马强,刘嘉,吴然嵩,马晓波.铜铟镓硒薄膜的真空制备工艺及靶材研究现状[J].功能材料,2013(14):1990-1994. |
| [3] | Ki W;Hillhouse H W .Earth-abundant element photovol-taics directly from soluble precursors with high yield u-sing a non-toxic solvent[J].Adv Energy Mater,2011,1(05):732-735. |
| [4] | 江丰,沈鸿烈,金佳乐,王威.Cu2ZnSnS4薄膜光电性能及其太阳电池的制备和研究[J].功能材料,2012(15):2040-2044. |
| [5] | Tsukasa Washio;Tomokazu Shinji;Shin Tajima .6% Efficiency Cu2ZnSnS4-based thin film solar cells using oxide precursors by open atmosphere type CVD[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2012(9):4021-4024. |
| [6] | FENG JIANG;HONGLIE SHEN;WEI WANG .Optical and Electrical Properties of Cu_(2)ZnSnS_(4) Film Prepared by Sulfurization Method[J].Journal of Electronic Materials,2012(8):2204-2209. |
| [7] | Tooru T;Akihiro Y;Daisuke S et al.Influence of compo-sition ratio on properties of Cu2 ZnSnS4 thin films fabrica-ted by co-evaporation[J].THIN SOLID FILMS,2010,518(21):S29-S33. |
| [8] | Shafaat A;Reuter K B;Oki G et al.A high efficiency electrodeposited Cu2 ZnSnS4 solar cell[J].Advanced Ener-gy Materials,2012,2(02):253-259. |
| [9] | Chao Gao;Honglie Shen;Feng Jiang;Hao Guan.Preparation of Cu_2ZnSnS_4 film by sulfurizing solution deposited precursors[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2012:189-192. |
| [10] | Maeda, K.;Tanaka, K.;Fukui, Y.;Uchiki, H. .Influence of H_2S concentration on the properties of Cu _2ZnSnS_4 thin films and solar cells prepared by solgel sulfurization[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2011(10):2855-2860. |
| [11] | V.G. Rajeshmon;C. Sudha Kartha;K.P. Vijayakumar;C. Sanjeeviraja;T. Abe;Y. Kashiwaba .Role of precursor solution in controlling the opto-electronic properties of spray pyrolysed Cu_2ZnSnS_4 thin films[J].Solar Energy,2011(2):249-255. |
| [12] | Guo, Qijie;Hillhouse, Hugh W.;Agrawal, Rakesh .Synthesis of Cu2ZnSnS4 Nanocrystal Ink and Its Use for Solar Cells[J].Journal of the American Chemical Society,2009(33):11672-11673. |
| [13] | Hironori Katagiri;Kazuo Jimbo;Win Shwe Maw;Koichiro Oishi;Makoto Yamazaki;Hideaki Araki;Akiko Takeuchi .Development Of Czts-based Thin Film Solar Cells[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2009(7):2455-2460. |
| [14] | Byungha Shin;Oki Gunawan;Yu Zhu .Thin film solar cell with 8.4% power conversion efficiency using an earth-abundant Cu_2ZnSnS_4 absorber[J].Progress in photovoltaics,2013(1):72-76. |
| [15] | Teodor K. Todorov;Jiang Tang;Santanu Bag;Oki Gunawan;Tayfun Gokmen;Yu Zhu;David B. Mitzi .Beyond 11% Efficiency: Characteristics of State-of-the-Art Cu_2ZnSn(S,Se)_4 Solar Cells[J].Advanced energy materials,2013(1):34-38. |
| [16] | Qijie Guo;Grayson M. Ford;Wei-Chang Yang;Charles J. Hages;Hugh W. Hillhouse;Rakesh Agrawal.Enhancing the performance of CZTSSe solar cells with Ge alloying[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2012:132-136. |
| [17] | 罗鹏,赵丽霞,徐键.Cu2ZnSnS4纳米颗粒及其薄膜的制备与表征[J].无机材料学报,2012(01):79-82. |
| [18] | Shi, L.;Pei, C.;Xu, Y.;Li, Q. .Template-directed synthesis of ordered single-crystalline nanowires arrays of Cu_2ZnSnS_4 and Cu_2ZnSnSe_4[J].Journal of the American Chemical Society,2011(27):10328-10331. |
| [19] | Yu Wang;Hao Gong .Cu_2ZnSnS_4 synthesized through a green and economic process[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2011(40):9627-9630. |
| [20] | P.A. Fernandes;P.M.P. Salome;A.F. da Cunha .Growth And Raman Scattering Characterization Of Cu_2znsns_4 Thin Films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2009(7):2519-2523. |
| [21] | Chesman A S R;Duffy N W;Peacock S et al.Non-injec-tion synthesis of Cu2 ZnSnS4 nanocrystals using a binary precursor and ligand approach[J].RSC Advances,2013,3(04):1017-1020. |
| [22] | Hiroyasu Nishi;Susumu Kuwabata;Tsukasa Torimoto .Composition-Dependent Photoelectrochemical Properties of Nonstoichiometric Cu2ZnSnS4 Nanoparticles[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2013(41):21055-21063. |
| [23] | Narayanasamy Sabari Arul;Dong Yeol Yun;Dea Uk Lee .Strong quantum confinement effects in kesterite Cu2ZnSnS4 nanospheres for organic optoelectronic cells[J].Nanoscale,2013(23):11940-11943. |
| [24] | Wei Wang;Honglie Shen;Xiancong He .Study on the synthesis and formation mechanism of Cu_2ZnSnS_4 particles by microwave irradiation[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2013(9):3140-3143. |
| [25] | Tai Guoan;Guo Wanlin .Sonochemistry-assisted micro-wave synthesis and optical study of single-crystalline CdS nanoflowers[J].Ultrasonics Sonochemistry,2008,15(04):350-356. |
| [26] | Jun He;Lin Sun;Kezhi Zhang;Weijun Wang;Jinchun Jiang;Ye Chen;Pingxiong Yang;Junhao Chu .Effect of post-sulfurization on the composition, structure and optical properties of Cu_2ZnSnS_4 thin films deposited by sputtering from a single quaternary target[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Jan.1):133-138. |
| [27] | Flynn, B.;Wang, W.;Chang, C.-H.;Herman, G.S. .Microwave assisted synthesis of Cu_2ZnSnS_4 colloidal nanoparticle inks[J].Physica status solidi, A. Applications and materials science ePSS,2012(11):2186-2194. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%