以核桃壳为碳源,微波辐射法制备了介孔活性炭。用XRD、SEM 和低温氮气吸脱附对所制备活性炭进行了物性分析；用恒流充放电、循环伏安和交流阻抗等方法分析了微波功率、辐射时间对活性炭电容性能的影响。确定活性炭的最佳制备工艺为微波功率480 W,辐射时间9 min。制得的活性炭平均孔径为4.44 nm,介孔率为78.51%,比表面积达1530 m2/g,为不规则、疏松多孔的无定形结构。当充放电电流为100 mA/g时,比电容为226.4 F/g,循环1000次后比电容为192.2 F/g,每次循环电容衰减仅为0.015%。
The mesoporous activated carbon was prepared by microwave radiation process using walnut shell as carbon source.The as-prepared activated carbon was well characterized by XRD,SEM and nitrogen adsorption-desorption.The influences of microwave power and radiation time on the capacitance characteristics of activated carbon for electrochemical capacitors was investigated by glavanostatic charge-discharge,cyclic voltammetry (CV)and AC impedance spectroscopy.Microwave power at 480 W and radiation time for 9 min were regarded as the optimum process.The activated carbon prepared under this process had the average pore size of 4.44 nm and the mesoporous rate of 78.51 %.The specific surface area was 1 530 m2/g and its shape was irregular,porous and amorphous structure.The specific capacitance was 226.4 F/g at the charge-discharge current of 100 mA/g. It kept 192.2 F/g after 1 000 cycles,and the capacity fade of activated carbon was only 0.015 % when cycled at 100 mA/g.
参考文献
| [1] | 王力臻,方华,张爱勤,张勇.微波辐射法制备竹炭电极材料[J].电池,2010(02):77-79. |
| [2] | Li Li Zhang;X. S. Zhao .Carbon-based materials as supercapacitor electrodes[J].Chemical Society Reviews,2009(9):2520-2531. |
| [3] | Da-Wei Wang;Feng Li;Min Liu .3D Aperiodic Hierarchical Porous Graphitic Carbon Material for High-Rate Electrochemical Capacitive Energy Storage[J].Angewandte Chemie,2008(2):373-376. |
| [4] | 王秀芳,张会平,陈焕钦.KOH活化法高比表面积竹质活性炭的制备与表征[J].功能材料,2006(04):675-679. |
| [5] | 李晶,赖延清,刘业翔.超级电容器碳电极材料的制备及性能[J].电池,2006(05):332-334. |
| [6] | Kirubakaran C J;Krishnaiah K;Seshadri S .Experimen-tal study of the production of activated carbon from coco-nut shells in a fluidized bed reactor[J].Industrial & En-gineering Chemistry Research,1991,30(11):2411-2416. |
| [7] | Guo Peizhi;Ji Qianqian;Zhang Lili et al.Preparation and characterization of peanut shell-based microporous carbons as electrode materials for supercapacitor[J].ACTA PHYSICO-CHIMICA SINICA,2011,27(12):2836-2840. |
| [8] | Yaokang Lv;Lihua Gan;Mingxian Liu;Wei Xiong;Zijie Xu;Dazhang Zhu;Dominic S. Wright .A self-template synthesis of hierarchical porous carbon foams based on banana peel for supercapacitor electrodes[J].Journal of Power Sources,2012(Jul.1):152-157. |
| [9] | Chao Peng;Xing-bin Yan;Ru-tao Wang;Jun-wei Lang;Yu-jing Ou;Qun-ji Xue.Promising activated carbons derived from waste tea-leaves and their application in high performance supercapacitors electrodes[J].Electrochimica Acta,2013:401-408. |
| [10] | 余琼粉,李明,宁平,易红宏,唐晓龙,陈玉保.核桃壳活性炭的制备及其在环境保护中的应用[J].化学工业与工程,2011(06):63-67,73. |
| [11] | Hu Z;Vansant E .Synthesis and characterization of a controlled-micropore-size carbonaceous adsorbent pro-duced from walnut shell[J].Microporous Materials,1995,3(06):603-612. |
| [12] | 宋天秀,丁士华,李胜,梁逵.微波加热法制备电极材料活性炭[J].电子元件与材料,2006(12):31-33. |
| [13] | 张利波,彭金辉,夏洪应,李玮,曲雯雯,朱学云.微波加热碳酸钾法制备烟杆基高比表面积活性炭[J].功能材料,2008(01):136-138. |
| [14] | A. G. Pandolfe;A. F. Hollenkamp .Carbon properties and their role in supercapacitors[J].Journal of Power Sources,2006(1):11-27. |
| [15] | C. Portet;P. L. Taberna;P. Simon;C. Laberty-Robert .Modification of Al current collector surface by sol-gel deposit for carbon-carbon supercapacitor applications[J].Electrochimica Acta,2004(6):905-912. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%