采用熔体单辊急冷法制备了非晶合金Fe52 Co34 Hf7 B6 Cu1薄带,在非晶合金制备过程中,铜辊表面线速度分别为49,45 m/s,合金中的元素 B 分别以纯 B 和 FeB 形式加入。研究表明,在同一冷速(49 m/s)的情况下,加入纯 B制备的非晶态合金的晶化激活能较加入 FeB 略高,其热稳定性较好;而同样加入FeB制备的非晶合金,冷速较快时(49 m/s)制备的非晶态合金晶化激活能较高,其热稳定性较好。
Amorphous ribbons Fe52 Co34 Hf7 B6 Cu1 were prepared using the single-roller melt-spinning technique. The surface linear velocity of copper wheel was 49m/s and 45m/s respectively.The adding manners of B in the amorphous are the pure B or compound FeB respectively.This research show that for the same cooling velocity 49 m/s,the crystallization activation energy of prepared amorphous alloy by injecting pure B was higher than the inj ecting FeB,and its thermal stability was higher too.For the same inj ecting FeB,the crystallization acti-vation energy of prepared amorphous alloy using 49 m/s cooling velocity was higher,and its thermal stability was better.
参考文献
[1] | B. Majumdar;S. Bysak;D. Akhtar .Nanocrystallization of soft magnetic Fe(Co)-Zr-B-Cu alloys[J].Journal of Magnetism and Magnetic Materials,2007(1):300-306. |
[2] | Willard MA.;Mchenry ME.;Thoma D.;Sickafus K.;Cross JO. Harris VG.;Laughlin DE. .Structure and magnetic properties of (Fe0.5Co0.5)(88)Zr7B4Cu1 nanocrystalline alloys[J].Journal of Applied Physics,1998(12):6773-6777. |
[3] | Kowalczyk M;Ferenc J;Liang Xiubing et al.Magnetic properties of HITPERM-type alloys at high temperature[J].Journal of Magnetism and Magnetic Materials,2006,304:e651. |
[4] | Tadeusz Kulik,梁秀兵,Jaroslaw Ferenc,徐滨士.纳米晶铁钴基软磁材料的研究[J].中国表面工程,2004(05):1-4,10. |
[5] | 周迎春,张启俭,晁月盛.非晶Fe78Si9B13合金磁致低温纳米晶化的超精细结构研究[J].功能材料,2010(10):1694-1698. |
[6] | Liang Xiubing;Tadeusz K;Ferenc J et al.M?ssbauer study on amorphous and nanocrystalline(Fe1-x Cox)86 Hf7B6Cu1 alloys[J].Materials Characterization,2006,58(02):143-147. |
[7] | Chao Yuesheng;Zhu Hanxian;Li Zhengming et al.Preparation and magneto-nanocrystallization of amor-phous alloy Fe60 Co26 Hf7 B6 Cu1[J].Journal of Physics,2009,188:012038. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%