以钛酸四异丙脂为原料,采用粒子型溶胶路线制备出稳定的 TiO2溶胶,通过浸渍涂膜法,在孔径为100 nm的管式Al2 O3微滤膜支撑体上制备出介孔TiO2膜。研究了介孔TiO2膜的制备过程对其完整性及孔结构的影响,同时考察了非负载介孔 TiO2膜对染料酸性橙7和亚甲基蓝的吸附性能。在溶胶中加入适量的 PVA 和 HPC,控制浸涂时间,在450℃焙烧1 h可获得完整的介孔TiO2膜,膜厚约0.5μm,孔径分布于3~10 nm。介孔TiO2膜对酸性橙7及亚甲基蓝吸附量随 pH 值变化,调节 pH 值可减少吸附造成的膜污染。
A stable TiO2 sol was synthesized from titanium isopropoxide by colloidal sol-gel route.Mesoporous TiO2 membranes were prepared with tubular Al2 O3 microfiltration membrane of 100 nm pore size as support by dip-coating method.The effect of preparation process on integrity and pore structure of mesoporous TiO2 mem-brane was studied in detail.In addition,the absorption of acid orange 7 and methylene blue onto unsupported mesoporous TiO2 membrane was researched.Defect-free mesoporous TiO2 membranes were obtained from TiO2 sol added appropriate amount of PVA and HPC as binder by time-controlled dip-coating followed by calci-nation at 450 ℃ for 1h.The thickness of TiO2 membrane was about 0.5μm and the pore size distributes in the range of 3-10 nm.The absorption of acid orange 7 and methylene blue onto mesoporous TiO2 membrane varies with pH value.It implies that adusting pH value may decrease membrane fouling caused by the adsorption.
参考文献
| [1] | Toshinori Tsuru .Inorganic porous membranes for liquid phase separation[J].Separation and Purification Methods,2001(2):191-220. |
| [2] | Keizo Nakagawa;Hideto Matsuyama;Masaaki Teramoto;Taisuke Maki;Noboru Kubota .Preparation of mesoporous silica membrane by solvent evaporation method for filtration application[J].Separation and Purification Technology,2005(2):145-151. |
| [3] | Zhang Lihui;Xu Mingxia;E Lei et al.Study on prepara-tion and properties of γ-Al2 O3 microporous film[J].Journal of Functional Materials,2004,35(09):2921-2924. |
| [4] | Toshinori Tsuru;Daisuke Hironaka;Yomohisa Yoshioka;Masashi Asaeda .Titania membranes for liquid phase separation: effect of surface charge on flux[J].Separation and Purification Technology,2001(1):307-314. |
| [5] | Ali Akbar Habibpanah;Sepideh Pourhashem;Hossein Sarpoolaky .Preparation and characterization of photocatalytic titania-alumina composite membranes by sol-gel methods[J].Journal of the European Ceramic Society,2011(15):2867-2875. |
| [6] | Aust U;Benfer S;Dietze M;Rost A;Tomandl G .Development of microporous ceramic membranes in the system TiO2/ZrO2[J].Journal of Membrane Science,2006(1/2):463-471. |
| [7] | Larbot A;Fabre J P;Guizard C et al.New inorganic ul-trafiltration membranes:titania and zirconia membranes[J].Journal of the American Ceramic Society,1989,72(02):257-261. |
| [8] | Wu Liqun;Huang Pei .Preparation of supported TiO2 ul-trafiltration membranes by sol-gel technique[J].Journal of Chemical Engineering of Chinese Universities,1999,13(03):205-210. |
| [9] | Zhang Yuzhi;Yu Yun;Song Lixin et al.Preparation and permeability of TiO2 ultrafiltration membranes[J].Journal of The Chinese Ceramic Society,2005,33(08):921-925. |
| [10] | 范苏,邱鸣慧,周邢,范益群.多通道TiO2超滤膜的制备及其在印染废水中的应用[J].南京工业大学学报（自然科学版）,2011(01):44-47. |
| [11] | Ali Alem;Hossein Sarpoolaky;Mehrdad Keshmiri .Titania ultrafiltration membrane: Preparation, characterization and photocatalytic activity[J].Journal of the European Ceramic Society,2009(4):629-635. |
| [12] | Voigt I;Stahn M;W?hner S et al.Integrated cleaning of coloured waste water by ceramic NF membranes[J].Separation and purification technology,2001,25(01):509-512. |
| [13] | Ralph Weber;Horst Chmiel;Valko Mavrov .Characteristics and application of new ceramic nanofiltration membranes[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2003(1/3):113-125. |
| [14] | 孙洪贵,夏海平,蓝伟光.分离膜材料的污染与清洗[J].功能材料,2002(01):26-28,32. |
| [15] | Kay A.;Gratzel M. .Dye-sensitized core-shell nanocrystals: Improved efficiency of mesoporous tin oxide electrodes coated with a thin layer of an insulating oxide[J].Chemistry of Materials,2002(7):2930-2935. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%