在 LSS(liquid-solid-solution)多相体系中制得了 CdSe、CdSe/ZnS 量子点和 Eu 掺杂的量子点.利用 TEM、XRD、PL、EDS 对产物进行了表征.TEM 结果显示所得的量子点形貌规则、尺寸均匀.XRD 结果显示 CdSe/ZnS 量子点呈六方晶系.PL 结果对比表明,合适厚度壳层 ZnS 包覆后的 CdSe 量子点发光效率明显提高,发光峰的半高宽有大幅度提高,并分析了所得的结果.掺杂稀土元素 Eu 后,CdSe(Eu)量子点在红光区域产生了新的发光峰；而 CdSe(Eu)/ZnS 量子点在红光区域内没有出现发光峰,并阐明了这种现象的原因.
CdSe,CdSe/ZnS and Eu doped QDs were synthesized in LSS system.The QDs were characterized by TEM,XRD,PL and EDS.The TEM results showed that the QDs had uniform size and morphology.And the results of XRD showed CdSe/ZnS QDs belonged to hexagonal crystal system.The PL of the samples proved that the CdSe QDs coated with suitable thickness ZnS had a remarkable rise in luminous efficiency and the FWHM (the full width half maximum).And we analyzed this results.The CdSe QDs doped with Eu had a new emission peak in red area,while the CdSe(Eu)/ZnS QDs did not.We also clarified the causes of this phenome-non .
参考文献
| [1] | Moeller G;Coe-Sullivan S .Quantum-DOT light-emitting device for displays[J].Information Display,2006,22(2):32-36. |
| [2] | Yeh DM;Huang CF;Lu YC;Yang CC .White-light light-emitting device based on surface plasmon-enhanced CdSe/ZnS nanocrystal wavelength conversion on a blue/green two-color light-emitting diode[J].Applied physics letters,2008(9):91112-1-91112-3-0. |
| [3] | 孙宝全,徐咏蓝,衣光舜,陈德朴.半导体纳米晶体的光致发光特性及在生物材料荧光标记中的应用[J].分析化学,2002(09):1130-1136. |
| [4] | Tang Aiwei;Teng Feng;Gao Yinhao .White light emis-sion from organic-inorganic hereto structure devices by using CdSe quantum dots as emitting layer[J].Journal of Luminescence,2007,122-123:649-651. |
| [5] | Chen HS;Lo B;Hwang JY;Chang GY;Chen CM;Tasi SJ;Wang SJJ .Colloidal ZnSe, ZnSe/ZnS, and ZnSe/ZnSeS quantum dots synthesized from ZnO[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2004(44):17119-17123. |
| [6] | Dingan Chen;Fei Zhao;Hang Qi .Bright and Stable Purple/Blue Emitting CdS/ZnS Core/Shell Nanocrystals Grown by Thermal Cycling Using a Single-Source Precursor[J].Chemistry of Materials: A Publication of the American Chemistry Society,2010(4):1437-1444. |
| [7] | 宁佳,王德平,黄文旵,姚爱华,郁美娟.CdSe量子点的制备及荧光性能改善[J].功能材料,2007(09):1531-1532,1536. |
| [8] | Xun Wang;Jing Zhuang;Qing Peng;Yadong Li .A general strategy for nanocrystal synthesis[J].Nature,2005(7055):121-124. |
| [9] | 杜保安,焦永静,李正平,倪,梅,严景丽.在多相体系中制备核壳型CdSe/ZnS量子点[J].材料导报,2009(06):100-102. |
| [10] | J.Nanda;D.D.Sarma .Size-Selected Zinc Sulfide Nanocrystallites:Synthesis,Structure,and optical Studies[J].Chemistry of Materials,2000(4):1018-1024. |
| [11] | 葛美英,魏调兴,吴杰,孙艳.Ⅱ-Ⅵ族核壳结构量子点的制备及其在生物方面的应用[J].上海有色金属,2012(01):20-24. |
| [12] | Reiss P;Protière M;Li Liang .Core/shell semiconductor nanocrystal[J].SMALL,2009,5(2):154-168. |
| [13] | 刘舒曼,徐征,刘峰奇,徐叙瑢.稀土掺杂ZnS纳米晶中稀土离子与纳米基质之间的能量传递[J].中国稀土学报,2001(06):566-569. |
| [14] | YUAN Xi-ming,XU Yong-sheng,YU Jiang-bo,WANG Yong-qian,WANG Hong-mei.Synthesis and Luminescence of Nano Fluorescent Powder of Y4Al2O9:Eu3+[J].武汉理工大学学报(材料科学版)英,2003(01):41-43. |
| [15] | Johannes R. Dethlefsen;Alexander A. Mikhailovsky;Peter T. Burks .Lanthanide Modification of CdSe/ZnS Core/Shell Quantum Dots[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2012(44):23713-23720. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%