首先借助种子乳液聚合手段，以苯乙烯、二乙烯苯为混合单体，在致孔剂存在下制备出壳具有微通道的聚苯乙烯核壳结构模板微球。利用该模板，通过毛细管力对导电聚合物单体进行充分吸附，利用溶液聚合制备了表面包覆均匀的有机导电聚合物(聚吡咯、聚苯胺)包覆聚苯乙烯复合微球，导电率达到5.5×10-5 S/cm左右。并成功利用水溶性很差、且在水体系中难以聚合的噻吩单体，通过相转移催化实现了对模板微球的包覆，得到表面形貌独特的聚噻吩包覆聚苯乙烯复合微球。
In this paper,polystyrene (PS)core-shell template particles with microchannels in shell were pre-pared through seed-polymerization by using mixed monomers of styrene (St)and divinyl benzene (DVB)with PS seeds emulsion firstly.Using the template particles,organic conductive polymers(OCPs)-coated PS com-posite particles were synthesized under capillary force through solution polymerization of polypyrrole (PPy)and polyaniline (PANI),and the conductivity of the particles was about 5.5×10-5S/cm.Furthermore,the nano-composite particle of PS/PTh was synthesized using thiophene(Th)chemical oxidative polymerization through phase transfer catalysis method.The overlayers of the core-shell PS/PTh composite spheres have diverse sur-face morphology.
参考文献
| [1] | Khan MA.;Armes SP. .Conducting polymer-coated latex particles[J].Advanced Materials,2000(9):671-674. |
| [2] | Lascelles S F;Armes S P;Zhdan P A et al.Surface characterization of micrometer-sized,polypyrrole-coated polystyrene latexes:verification of a 'core-shell ' mor-phology[J].Journal of Materials Chemistry,1997,7(08):1349-1355. |
| [3] | Lascelles S F;Armes S P .Synthesis and characterization of micrometer-sized,polypyrrole-coated polystyrene late-xes[J].Journal of Materials Chemistry,1997,7(08):1339-1347. |
| [4] | Barthet C.;Lascelles SF.;Luk SY.;Stanley HME.;Armes SP. .Synthesis and characterization of micrometer-sized, polyaniline-coated polystyrene latexes[J].Langmuir: The ACS Journal of Surfaces and Colloids,1998(8):2032-2041. |
| [5] | Khan M A;Armes S P .Synthesis and characterization of micrometer-sized poly(3,4-ethylenedioxythiophene)-coa-ted polystyrene latexes[J].Langmuir,1999,15:3469-3475. |
| [6] | Park MK.;Onishi K.;Locklin J.;Caruso F.;Advincula RC. .Self-assembly and characterization of polyaniline and sulfonated polystyrene multilayer-coated colloidal particles and hollow shells[J].Langmuir: The ACS Journal of Surfaces and Colloids,2003(20):8550-8554. |
| [7] | Cairns DB.;Khan MA.;Perruchot C.;Riede A.;Armes SP. .Synthesis and characterization of polypyrrole-coated poly(alkyl methacrylate) latex particles[J].Chemistry of Materials,2003(1):233-239. |
| [8] | Syuji Fujii;Steven P.Armes;Richard Jeans;Robin Devonshire;Samantha Warren .Synthesis and Characterization of Polypyrrole-Coated Sulfur-Rich Latex Particles:New Synthetic Mimics for Sulfur-Based Micrometeorites[J].Chemistry of Materials: A Publication of the American Chemistry Society,2006(11):2758-2765. |
| [9] | 杨正龙,侯文博,刘正平,黄俐研,彭笑刚.单分散核/壳结构导电高分子复合材料的研究（Ⅰ）--分散核/壳结构聚苯乙烯/聚吡咯的结构表征[J].高等学校化学学报,2002(10):2014-2016. |
| [10] | 黄俐研,杜江,刘正平.壳层可控导电聚吡咯/聚苯乙烯复合微球及聚吡咯中空微胶囊的制备[J].高等学校化学学报,2005(06):1186-1188. |
| [11] | Huang J;Virji S;Weiller B H et al.Polyaniline nano-fibers:facile synthesis and chemical sensors[J].Journal of the American Chemical Society,2003,125:314-315. |
| [12] | Jiaxing Huang;Richard B.Kaner .Nanofiber Formation in the Chemical Polymerization of Aniline:A Mechanistic Study[J].Angewandte Chemie,2004(43):5817-5821. |
| [13] | 陆胜,方鸣,肖建惠.高分子导电聚合物PEDT化学聚合过程及结构性能研究[J].功能材料,2012(21):2912-2916. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%