在金属表面制备高硬度、耐磨损且摩擦系数低的功能涂层,可以有效减少摩擦功耗,延长机械设备的使用寿命。采用化学复合镀方法,在不锈钢基质上实现Ni-W-P-SiC-WS2镀层的镀覆,并对镀层的表面形貌、微观结构、成分、硬度、摩擦学性能和耐蚀性等进行了测试和分析,研究结果表明,Ni-W-P-SiC-WS2镀层表面平整,由胞状物和分布均匀的复合颗粒组成；镀层中P的含量在5%~8%之间,属于中磷镀层。与同等实验条件下的二元合金镀层 Ni-P-SiC-WS2镀层相比,由于 W的共沉积,三元合金镀层 Ni-W-P-SiC-WS2的微观硬度、腐蚀性能和耐磨性均有所提高,同时自润滑性能更加优异。
The functional coating owning high microhardness,wear resistance and low friction coefficient on metal surface can reduce friction power consumption and prolong the service life of mechanical equipment.Ni-W-P-SiC-WS2 composite coatings were deposited on the stainless steel substrate by electroless plating in this pa-per.Meanwhile,the surface morphology,microstructure,composition,microhardness,tribological properties and corrosion resistance were tested and analyzed.Results showed that the surface of Ni-W-P-SiC-WS2 coatings were smooth and composite particles distribute uniformly.The phosphorus content of the coating ranges from 5% to 8% and belongs to medium phosphoric coating.By comparison with Ni-P-SiC-WS2 ,the microhardness, corrosion and wear resistance of ternary alloy coating Ni-W-P-SiC-WS2 were greatly improved because of the co-deposited tungsten.Moreover,the lubricating properties of the coating were more outstanding.
参考文献
| [1] | 俞世俊,宋力昕,黄银松,赵荣根,胡行方.化学镀Ni-P-SiC复合镀层的研究[J].无机材料学报,2004(03):647-652. |
| [2] | Prasanta Sahoo;Suman Kalyan Das .Tribology of electroless nickel coatings - A review[J].Materials & design,2011(4):1760-1775. |
| [3] | H. Bi;K.C. Kou;A.E. Rider;K. Ostrikov;H.W. Wu;Z.C. Wang .Low-phosporous nickel-coated carbon microcoils: Controlling microstructure through an electroless plating process[J].Applied Surface Science,2009(15):6888-6893. |
| [4] | M. Palaniappa;S. K. Seshadri .Friction and wear behavior of electroless Ni-P and Ni-W-P alloy coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2008(5/6):735-740. |
| [5] | W.L. Liu;S.H. Hsieh;W.J. Chen;Y.C. Hsu .Growth Behavior Of Electroless Ni-co-p Deposits On Fe[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(6):3880-3883. |
| [6] | 朱绍峰,吴玉程,黄新民.化学沉积Ni-Zn-P合金及其冲蚀特性[J].功能材料,2010(07):1181-1185. |
| [7] | 徐扬,邹勇,栾涛.镀层Cu含量对Ni-P-Cu镀层性能及电化学行为的影响[J].功能材料,2013(02):244-248. |
| [8] | Ranganatha S;Venkatesha T V;Vathsala K .Electroless Ni-W-P coating and its nano-WS2 composite[J].Prepara-tion and Properties,2012,51:7932-7940. |
| [9] | Zhao Q.;Liu Y.;Muller-Steinhagen H.;Liu G. .Graded Ni-P-PTFE coatings and their potential applications[J].Surface & Coatings Technology,2002(2/3):279-284. |
| [10] | Wan Changsun .The effect of Al2 O3 concentration on properties of Ni-W-P-Al2 O3 electroless composite Coat-ing[J].Current Advances in Materials and Processes,2012,468-471:1163-1166. |
| [11] | 胡国信.21 世纪化学镀镍技术[A].上海,2000:1-8. |
| [12] | Gu CD;Lian JS;Li GY;Niu LY;Jiang ZH .High corrosion-resistant Ni-P/Ni/Ni-P multilayer coatings on steel[J].Surface & Coatings Technology,2005(1):61-67. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%