以1.5%异氰酸酯(MDI)界面改性剂改性处理后的竹纤维和聚乳酸为原料,通过注射成型工艺制备竹纤维增强聚乳酸复合材料,探讨竹纤维质量分数对复合材料界面、力学性能、吸水率、热性能的影响。结果表明,随着竹纤维质量分数的增加,复合材料拉伸强度、冲击强度、存储模量以及热稳定性均先增大后减小,24h吸水率逐渐增大,损耗因子逐渐降低。竹纤维质量分数为50%时,复合材料的拉伸强度和冲击强度分别达到最大值63.2MPa和11.6kJ/m2,复合材料存储模量最大,热稳定性最好。
Bamboo fiber reinforced polylactic acid composites was prepared by inj ection molding technology with polylactic acid and the bamboo fiber modified with 1 .5% isocyanate (MDI)interfacial modifier.Effect of BF mass fraction on interface,mechanical property,water absorption and thermal property of composites were in-vestigated.The results showed that tensile strength,impact strength,storage modulus and thermal stability of composites first increased and then decreased with increase of BF mass fraction,24h water absorption gradually increased,loss factor gradually increased.When BF mass fraction was 50%,tensile strength and impact strength of composites arrived the maximum of 63.2MPa and 11.6kJ/m2 ,respectively,composites presented the highest storage modulus and the best the thermal stability.
参考文献
| [1] | Das M;Chakraborty D .Influence of alkali treatment on the fine structure and morphology of bamboo fibers[J].Journal of Applied Polymer Science,2006(5):5050-5056. |
| [2] | Das M;Chakraborty D .Evaluation of improvement properties of bamboo fibers of physical and mechanical due to alkali treatment[J].Journal of Applied Polymer Science,2008(1):522-527. |
| [3] | K. Oksman;M. Skrifvars;J.-F. Selin .Natural fibres as reinforcement in polylactic acid (PLA) composites[J].Composites science and technology,2003(9):1317-1324. |
| [4] | Shbata S;Cao Y;Fukumoto I .Fabrication of composites made from kenaf fiber and biodegradable resin by a hot press and the flexural properties[J].Transactions of the Japan Society of Mechanical Engineers,2006,72:676-714. |
| [5] | 曹勇,合田公一,吴义强,陈鹤梅.洋麻纤维增强全降解复合材料的制备及其弯曲模量[J].复合材料学报,2007(03):28-34. |
| [6] | Nishino T;Hirao K;Kotera M et al.Kenaf reinforced bi-odegradable composite[J].Composites Science and Technology,2003,63:1281-1285. |
| [7] | 华晋,赵志敏,余伟,王田虎.聚乳酸/木粉复合材料的力学及吸水性能研究[J].功能材料,2011(10):1762-1764,1767. |
| [8] | Shbata S;Cao Y;Fukumoto I .Press forming of short nat-ural fiber-reinforced biodegradable resin:effects of fiber volume fraction and length on the flexural properties[J].Polymer Testing,2005,24(08):100-105. |
| [9] | Shbata S;Fukumoto I;Cao Y .Effects of fiber compression and length distribution on the flexural properties of short kenaf fiber-reinforced biodegradable composites[J].Polymer Composites,2006,27(02):170-174. |
| [10] | Dash B N;Rana A K;Mishra H K et al.Novel,low-cost j ute-polyester composites.Part 1:processing,me-chanical properties,and SEM analysis[J].Polym Com-pos,1999,20:62-71. |
| [11] | 梁基照.无机粒子填充聚合物复合材料的储能模量及其表征[J].华南理工大学学报（自然科学版）,2008(11):143-146. |
| [12] | Y. Cao;S. Shibata;I. Fukumoto .Mechanical properties of biodegradable composites reinforced with bagasse fibre before and after alkali treatments[J].Composites, Part A. Applied science and manufacturing,2006(3):423-429. |
| [13] | A. A. Yussuf;I. Massoumi;A. Hassan .Comparison of Polylactic Acid/Kenaf and Polylactic Acid/Rise Husk Composites: The Influence of the Natural Fibers on the Mechanical, Thermal and Biodegradability Properties[J].Journal of polymers and the environment,2010(3):422-429. |
| [14] | Takashi Nishino;Koichi Hirao;Masaru Kotera .Kenaf reinforced biodegradable composite[J].Composites science and technology,2003(9):1281-1286. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%