采用高温烧结固相反应法制备了钙钛矿结构锰化合物热控涂层。利用变温场稳态卡计法半球热辐射率测试设备研究了热控涂层的红外半球发射率和温度之间的关系。结果表明该化合物在低温条件下表现为低热辐射率特性，在高温表现为高热辐射率特性。此外，还对该热控涂层进行了真空-紫外、真空-质子、真空-电子辐照、热循环、真空-放气等空间环境模拟实验，实验表明这种智能涂层具有良好的空间稳定性。说明该热控涂层在未来的航天器上具有广阔的应用前景。
Perovskite structure manganese oxide thermal control coatings were synthesized by solid-state reac-tion method.The relationship between the total hemispherical emittance (εH )and the temperature of the ther-mal control coatings was measured on a calorimetric emissometer which was based on the steady state calorime-tric method.The compounds show thermochromic properties andεH have low value at low temperature and have high value at high temperature.Environmental adaptability tests such as ultraviolet irradiation test,pro-ton irradiation test,electron irradiation test,thermal cycle test,outgassing test were conducted also.The test results showed that thermal control coatings had very good space stability performance,which made the ther-mal control coatings attractive as potential active thermal control materials for future satellites.
参考文献
| [1] | 闵桂荣.航天器热控制[M].北京:科学出版社,1998 |
| [2] | 侯增祺;胡金刚.航天器热控制技术[M].北京:中国科学技术出版社,2007 |
| [3] | Kruzelecky R V;Haddad E et al.Thin-film smart radia-tor tiles with dynamically tuneable thermal emittance 2005-01-2906[R].San Antonio |
| [4] | Theodore D. Swanson;Gajanana C. Birur .NASA thermal control technologies for robotic spacecraft[J].Applied thermal engineering: Design, processes, equipment, economics,2003(9):1055-1065. |
| [5] | Chandrasekhar P.;Zay BJ.;McQueeney T.;Scara A.;Ross D.;Birur GC. Haapanen S.;Kauder L.;Swanson T.;Douglas D. .Conducting Polymer (CP) infrared electrochromics in spacecraft thermal control and military applications[J].Synthetic Metals,2003(1/3):23-24. |
| [6] | 胡晓红,李伟信,张跃,徐惠彬.特种光谱选择性涂层的遗传算法优化设计[J].功能材料,2004(z1):1684-1687. |
| [7] | Sigel R;Howell J R.Thermal radiation heat transfer[M].New York:Hemisphere Publishing Corp,1981 |
| [8] | Shimakawa Y;Yoshiake T;Kubo T.Avariable-emit-tance radiator based on a metal-insulator transition of (La,Sr)MnO3 thin films[J].Applied Physics Letters,2002(80):4864-4868. |
| [9] | K. Shimazaki;A. Ohnishi;Y. Nagasaka .Development of spectral selective multilayer film for a variable emittance device and its radiation properties measurements[J].International Journal of Thermophysics,2003(3):757-769. |
| [10] | Sumitaka Tachikawa;Akira Ohnishi;Yuichi Shimakawa;Atsushi Ochi;Akira Okamoto;Yasuyuki Nakamura .Development of a Variable Emittance Radiator Based on a Perovskite Manganese Oxide[J].Journal of thermophysics and heat transfer,2003(2):264-268. |
| [11] | Jiang X.Development of La1-xSrxMnO3 thermo-chromic coating for smart spacecraft thermal radiator ap-plication[A].Collioure,2006 |
| [12] | Ochi A;Mori T;Shimakawa Y.Variable thernal-emittance radiator using La1-x Srx MnO3 thick film on PSZ substrate[J].Key Engineering Materials,2004(269):129-132. |
| [13] | 章俞之;唐根初;于 云.变温状态下材料半球发射率测量方法研究[A].上海,2011:152-157. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%