半固态触变成形过程对保证成形后零件良好的组织和性能起着至关重要的作用,通过观测半固态成形前后组织之间的联系可知,压铸过程中的成形状况和压铸前的组织特征均影响压铸后零件的组织和性能,半固态加热和压铸成形这2个阶段存在一定的联系.这些对于半固态成形的质量控制具有一定的指导意义.
参考文献
| [1] | Spencer D B;Mehrabian R;Flemings M C .Rheological Behavior of Sn-15 Pct Pb in the Crystallization Range[J].Metallurgical and Materials Transactions,1972,3:1925-1932. |
| [2] | Shibata R;Kaneuchi T;Soda T.New semi-liquid casting process[A].Sheffield England,1996:296-302. |
| [3] | 吴炳尧.半固态金属铸造工艺研究及发展前景[J].铸造,1999(03):45. |
| [4] | Kirwood D H .Semi-solid metal forming[J].International Materials Reviews,1994,39(05):173. |
| [5] | Nussbaum A I.Semi-solid forming of aluminum and magnesium[J].Light Metals Age,1996(06):6. |
| [6] | 杨湘杰,韩丽华,谢水生.铝合金触变成形技术及其应用[J].江西科学,1999(04):261-267. |
| [7] | 康永林;毛卫民;胡壮麒.金属材料半固态加工理论与技术[M].北京:科学出版社,2004:218. |
| [8] | Yang Yitao;Wang Jianfu;Chen Meng et al.Semi-solid thixocasting structure of aluminum alloy and relevant assistant analysis with the help of computer simulation[J].Frontiers of Materials Science in China,2008,36(02):306-310. |
| [9] | 王建甫,杨弋涛,张恒华,邵光杰.A357半固态初生相在二次加热和成形过程中的演变行为[J].特种铸造及有色合金,2008(03):189-192. |
| [10] | 杨弋涛,余中士,张恒华,孙宝良,邵光杰.计算机模拟在铝合金半固态压铸中的应用[J].特种铸造及有色合金,2006(07):417-419. |
| [11] | 王建甫 .A356/A357铝合金半固态成型工艺性能分析及其模拟[D].上海大学,2008. |
| [12] | 杨红亮,张质良,I.Ohnaka,H.Yasuda,A.Sugiyama,T.Ohmichi.ZL101合金半固态二次加热[J].中国有色金属学报,2003(03):626-630. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%