对X80管线钢埋弧焊焊接接头进行了-80~20℃温度范围的夏比冲击实验.测试了其冲击吸收功和脆性断面率,用扫描电镜观察了其断口形貌,分析了焊接接头断裂形式和断口形貌,讨论了焊接接头的韧脆转变温度和冲击断裂的力学行为.结果表明,室温时断口为韧窝状分布,焊接接头的韧脆转变温度为-28℃;断口形貌由韧性断裂向脆性断裂转变,断口主要表现为解理断裂.

参考文献

[1] HWANGB;LEES;KIMYM et al.Analysis of abnormal frac ture occur ring during drop-weight tear test of high-toughness line-pipeline steel[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,368(01):18-27.
[2] X.B. Yang;Z. Zhuang;X.C. You .Dynamic fracture study by an experiment/simulation method for rich gas transmission X80 steel pipelines[J].Engineering Fracture Mechanics,2008(18):5018-5028.
[3] Y.M. KIM;S.K. KIM;Y.J. LIM .Effect of Microstructure on the Yield Ratio and Low Temperature Toughness of Linepipe Steels[J].ISIJ International,2002(12):1571-1577.
[4] SANG Y S;BYOUNGCHUL H;SUNGBAK L et al.Correlation of microstructure and charpy impact properties in API X70 and X80 pipeline steels[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,458(01):281-289.
[5] 胥聪敏.X80钢在霍尔果斯水饱和土壤中的短期腐蚀行为研究[J].材料工程,2011(03):78-81,86.
[6] Sung, H.K.;Shin, S.Y.;Cha, W.;Oh, K.;Lee, S.;Kim, N.J. .Effects of acicular ferrite on charpy impact properties in heat affected zones of oxide-containing API X80 linepipe steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(9):3350-3357.
[7] 周民,杜林秀,刘相华,王悦新.不同温度下X100管线钢的冲击韧性[J].塑性工程学报,2010(05):108-113.
[8] 张小立,庄传晶,吉玲康,冯耀荣,赵文轸,霍春勇.高钢级管线钢的特征参量及其与强韧性的关系[J].材料工程,2006(08):3-7.
[9] T.F.A. Santos;T.F.C. Hermenegildo;C.R.M. Afonso;R.R. Marinho;M.T.P. Paes;A.J. Ramirez .Fracture toughness of ISO 3183 X80M (API 5L X80) steel friction stir welds[J].Engineering Fracture Mechanics,2010(15):2937-2945.
[10] 李红英,魏冬冬,林武,曾翠婷,宾杰.X80管线钢冲击韧性研究[J].材料热处理学报,2010(11):73-78.
[11] 张莉莉,张骁勇,高惠临,王锋.一种高铌X80管线钢的组织性能分析[J].材料工程,2009(05):1-5.
[12] 衣海龙,杜林秀,王国栋,刘相华.X80管线钢的组织与性能研究[J].东北大学学报(自然科学版),2008(02):213-216.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%