在国产离子镀和空心阴极离子镀复合镀膜机上,通过改变脉冲偏压值制备了(Ti,Al)N涂层.用X射线衍射仪对涂层的相组成进行了检测分析,并通过测得的衍射谱线计算了(Ti,Al)N涂层中的残余应力值；扫描电镜观察涂层表面微观形貌显示涂层表面存在“大颗粒”现象；用材料表面微纳米力学测试系统检测了涂层与基体间的结合力和涂层的硬度值.对涂层中残余应力与质量和性能之间关系的研究分析表明:(Ti,Al)N涂层中存在着残余压应力,且随脉冲偏压值的增加其值有先减小后增大的趋势；涂层中“大颗粒”现象随脉冲偏压值的提高能够显著得到减轻,涂层与基体间结合力得到提高,涂层的硬度值增大,涂层质量和力学性能均得到改善.
参考文献
| [1] | Torres, R.D.;Soares, P.C.;Schmitz, C.;Siqueira, C.J.M. .Influence of the nitriding and TiAlN/TiN coating thickness on the sliding wear behavior of duplex treated AISI H13 steel[J].Surface & Coatings Technology,2010(5):1381-1385. |
| [2] | 袁建鹏,刘富荣,于月光.Al含量对多弧离子镀Ti1-xAlxN涂层微观结构及性能的影响[J].有色金属,2009(04):26-29. |
| [3] | WU H;SONG L;SUN Y G.Influence of hollow cathode electron beam on TiAlN films prepared by multi-arc ion plating[J].Current Advances in Materials and Processes,2011(314-316):209-213. |
| [4] | 蒋钊,陈学康.薄膜的应力控制技术研究现状[J].真空科学与技术学报,2008(z1):17-21. |
| [5] | 黄自谦,贺跃辉,蔡海涛,肖逸锋,黄伯云.TiAlN涂层的热残余应力分析[J].中国有色金属学报,2007(06):897-902. |
| [6] | Bielawski M .Residual stress control in TiN/Si coatings deposited by unbalanced magnetron sputtering[J].Surface & Coatings Technology,2006(12/13):3987-3995. |
| [7] | 弓满锋,乔生儒,卢国锋,姬浩.X射线测量高速钢上不同厚度氮化钛涂层残余应力[J].材料科学与工艺,2010(03):415-419,424. |
| [8] | Knutsson, A.;Johansson, M.P.;Karlsson, L.;Odén, M. .Machining performance and decomposition of TiAlN/TiN multilayer coated metal cutting inserts[J].Surface & Coatings Technology,2011(16):4005-4010. |
| [9] | 卢龙,蒋涛,严铿.基体负偏压对TiAlN/TiN膜层组织成分及硬度的影响[J].热加工工艺,2009(24):78-80,83. |
| [10] | C.-L. Chang;J.-Y. Jao;T.-C. Chang .Influences of bias voltage on properties of TiAl-doped DLC coatings synthesized by cathodic arc evaporation[J].Diamond and Related Materials,2005(11/12):2127-2132. |
| [11] | E. Vogli;W. Tillmann;U. Selvadurai-Lassl;G. Fischer;J. Herper .Influence of Ti/TiAlN-multilayer designs on their residual stresses and mechanical properties[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2011(20):8550-8557. |
| [12] | Ahlgren, M;Blomqvist, H .Influence of bias variation on residual stress and texture in TiAIN PVD coatings[J].Surface & Coatings Technology,2005(1/4):157-160. |
| [13] | Abadias G .Stress and preferred orientation in nitride-based PVD coatings[J].Surface & Coatings Technology,2008(11):2223-2235. |
| [14] | YONGQW;CHUN Z G .Effects of pulsed bias duty ratio on microstructure and mechanical properties of TiN/TiAlN multilayer coatings[J].Applied Surface Science,2011,257(17):7881-7886. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%