采用喷射-沉淀法成功地制备了纳米晶Ni1-xZnxFe2O4(0≤x≤1.0)铁氧体粉料.通过TG- DSC,XRD,TEM等测试手段分析了其微观结构和形貌,用振动样品磁强计测量其室温下磁性能.结果表明:喷射-共沉淀法制备的粉料颗粒细小均匀、形状完整.600℃下煅烧1.5h,样品晶粒尺寸为30nm左右,平均颗粒尺寸小于100nm.随着Zn2+含量的增加,Ni-Zn铁氧体的晶胞参数逐渐增大.室温下,样品比饱和磁化强度随Zn2+含量增加而增加,当x=0.5mol时,最大比饱和磁化强度Ms为66.8A·m2 ·kg-1.
参考文献
| [1] | Dormann JL.;Fiorani D. .NANOPHASE MAGNETIC MATERIALS - SIZE AND INTERACTION EFFECTS ON STATIC AND DYNAMICAL PROPERTIES OF FINE PARTICLES[J].Journal of Magnetism and Magnetic Materials,1995(1):415-418. |
| [2] | R.H. Kodama .magnetic nanoparticles[J].Journal of Magnetism and Magnetic Materials,1999(1/3):359-372. |
| [3] | Zhenxing Yue;Ji Zhou;Longtu Li .Synthesis of nanocrystalline NiCuZn ferrite powders by sol-gel auto-combustion method[J].Journal of Magnetism and Magnetic Materials,2000(1/2):55-60. |
| [4] | BUSCHOW K H J.Handbook of Magnetic Materials[M].Amsterdam:North-Holland Co,2003 |
| [5] | 庞利佳,孙光飞,陈菊芳,梁家欢,张锦标,黎文安.纳米复合Pr2Fe14B/α-Fe永磁材料晶化行为和磁性能的研究[J].材料工程,2007(01):3-6. |
| [6] | 曹茂盛,刘海涛,陈玉金,王彪,朱静.Synthesis process and growth mechanism of γ′-Fe4N nanoparticles by phase-transformation[J].中国科学E辑(英文版),2003(01):104-112. |
| [7] | C. Suryanarayana .Nanocrystalline materials[J].International Materials Reviews,1995(2):41-64. |
| [8] | 关飞飞,姚兰芳,谢伏将,田琳琳,方学玲,卜胜利.纳米α-Fe2O3/SiO2复合材料的制备及磁性能[J].材料工程,2008(10):254-256. |
| [9] | 张立德;牟季美.纳米材料和纳米结构[M].北京:科学出版社,2001 |
| [10] | 李梦龙.化学数据速查手册[M].北京:化学工业出版社,2003 |
| [11] | 李萌远;李国栋.铁氧体物理学[M].北京:科学出版社,1978 |
| [12] | SELLMYER D J;LIU Y;SHINDO D.Handbook of Advanced Magnetic Materials[M].北京:清华大学出版社,2005 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%