通过机械合金化制备了成分(质量分数/％)为Fe- 14Cr-0.5Ti-0.35Y2O3的氧化物弥散强化合金粉末,机械合金化后粉末内部各合金元素分布均匀.采用热等静压的方法制得14CrODS铁索体钢,并对其进行锻造和热处理.与未添加氧化物弥散颗粒的14CrNA相比,14CrODS钢的强度有明显提高,但是与MA957有一定差距,抗拉强度有待改进；与MA957相比,14CrODS表现出良好的塑性,锻造可进一步提高14CrODS的高温塑性,但是锻造过程中的残余应力使材料低温拉伸时呈脆性,退火可去除残余应力,极大地提高14CrODS的塑性,使其远优于MA957.
参考文献
| [1] | OKSIUTA Z;BALUC N .Microstructurc and Charpy impact propcrtics of 12-14Cr oxide dispersion-strengthened ferritic steels[J].Journal of Nuclcar Materials,2008,374(1-2):178-184. |
| [2] | 柳光祖,田耘,单秉权,李华林,汤咏舫,刘勇.ODS高温合金[J].材料科学与工程学报,2000(z1):25-28. |
| [3] | Sokolov MA;Hoelzer DT;Stoller RE;McClintock DA .Fracture toughness and tensile properties of nano-structured ferritic steel 12YWT[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2007(a):213-216. |
| [4] | AI.AMO A;LAMBARD V;AVERTY X et al.Asscssment of ODS-14％Cr ferritic alloy for high temperature applications[J].Journal of Nuclear Materials,2004,329 330:333-337. |
| [5] | J. Henry;X. Averty;Y. Dai;J.P. Pizzanelli;J.J. Espinas.Tensile properties of ODS-14%Cr ferritic alloy irradiated in a spallation environment[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2009:345-348. |
| [6] | CHO H S;KIMURA A .Corrosion rcsistancc of high-Cr oxide dis persion strcngthcncd ferritic stecls in super-critical pressurized water[J].Journal of Nuclear Matcrials,2007,867-370:1180-1184. |
| [7] | 陈振华;陈鼎.机械合金化与固液反应球磨[M].北京:化学工业出版社,2006:66-68. |
| [8] | 何培,周张健,李明,许迎利,葛昌纯.机械合金化对ODS铁素体钢粉末的微观形貌和结构的影响[J].北京科技大学学报,2009(07):836-841. |
| [9] | Klueh RL;Shingledecker JP;Swindeman RW;Hoelzer DT .Oxide dispersion-strengthened steels: A comparison of some commercial and experimental alloys[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2005(2/3):103-114. |
| [10] | 航空航天工业部航空装备失散分析中心.金属材料断口分析及图谱[M].北京:科学出版社,1991:27-28. |
| [11] | 陈畅,汪明朴,金鹏,张娟,郭明星,谭望.退火温度对镦粗纯钼棒组织和横向塑性的影响[J].中国有色金属学报,2009(06):1061-1067. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%