采用TiZrNiCu合金作为中间层材料研究了Ti3Al基合金与Ti-6Al-4V合金的瞬间液相(TLP)扩散连接接头成分、组织转变及显微硬度.研究结果表明,连接温度和连接时间对接头成分和组织有较大的影响.随着连接温度的提高和连接时间的延长,接头中元素分布趋于均匀,连接区宽度增大.连接温度为850℃和900℃时,液相的残留使得接头中存在Ti-Cu金属间化合物.当连接温度为950℃,连接时间为30min时,等温凝固的完成使Ti-Cu金属间化合物从接头中消失.随着连接温度的提高和连接时间的延长,接头连接区硬度降低.当连接温度为950℃,连接时间为30min时,接头硬度分布较均匀.
参考文献
| [1] | Kim JS;Shin DH;Chang YW;Lee CS .Constitutive analysis on superplastic deformation mechanisms of two-phase Ti3Al-xNb alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):117-125. |
| [2] | Dutkiewicz J.;Maziarz W.;Heinrich H.;Kostorz G. .Structure of Ti-Al-Nb intermetallics produced by mechanical alloying and hot-pressing techniques[J].Materials Chemistry and Physics,2003(2/3):414-416. |
| [3] | WARD-CLOSE C M;MINORB R;DOORBARB P J .Intermetallic-matrix composites-a review[J].Intermetallics,1996,4(03):217-229. |
| [4] | L Maruyama;M. Yamaguchi;G. Suzuki .Effects of lamellar boundary structural change on lamellar size hardening in TiAl alloy[J].Acta materialia,2004(17):5185-5194. |
| [5] | V. Maurice;G. Despert;S. Zanna .XPS study of the initial stages of oxidation of alpha_2-Ti_3Al and gamma-TiAl intermetallic alloys[J].Acta materialia,2007(10):3315-3325. |
| [6] | 陈波,熊华平,毛唯,程耀永,吴欣,叶雷.采用Ti-15Cu-15Ni真空钎焊Ti3Al基合金[J].电焊机,2008(09):73-75. |
| [7] | 王国庆,赵玥,吴爱萍,邹贵生,任家烈.Ti3Al合金激光焊接接头高温拉伸性能及显微组织[J].中国有色金属学报,2007(11):1803-1807. |
| [8] | P. JJCAI;W. HUIQIANG;H. JINGSHAN .Microstructure evolution of electron beam welded Ti_3Al-Nb joint[J].Materials Characterization,2005(2):99-105. |
| [9] | BULENT K;NURI O;ERTAN E et al.Diffusion bonding between Ti-6Al-4V alloy and ferritic stainless steel[J].Materials Letters,2007,61:1747-1750. |
| [10] | ORHAN N;KHAN T I;EROGLU M .Diffusion bonding of a microduplex stainless steel to Ti-6Al-4V[J].Scripta Materialia,2001,45:441-446. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%