对航空MDYB-3定向有机玻璃不同温度下的蠕变行为进行了试验研究.得到了有机玻璃在20,50℃和75℃和不同应力下的蠕变曲线,结果表明:有机玻璃蠕变分为三个阶段,随着温度和应力的增大,有机玻璃的蠕变速率加快,蠕变断裂伸长增大,抗蠕变断裂时间变短.运用陈化理论,Norton公式和指数公式分别描述了蠕变三个阶段的特性.
Creep behaviors of aeronautic Polymethyl Methacrylate (MDYB-3 PMMA) under different temperatures were experimentally investigated. The creep curves of PMMA at 20℃,50℃ and 75℃ and with various stresses were obtained. It was indicated that the duration curves of creep could be divided into three phases. Experimental results showed that the steady creep accumulation speed was increasing with the temperature and stress increasing, and the rupture stretch was increasing accordingly, but the failure time was reducing. The Chen theory, Norton formula and exponential expression were used to describe three phases of creep behaviors respectively.
参考文献
| [1] | 马丽婷,陈新文,苏彬.航空有机玻璃老化研究进展[J].材料工程,2004(08):57-59,64. |
| [2] | 朱锡雄;朱国瑞.高分子材料强度学[M].杭州:浙江大学出版社,1992 |
| [3] | 李之达,张通,黄豪.PMMA一维蠕变的实验研究[J].武汉理工大学学报(交通科学与工程版),2004(01):5-7,25. |
| [4] | ZHENG S F;WENG G J .A new constitutive equation for the long-term creep of polymers based on physical aging[J].European Journal of Mechanics A/Solids,2002,21:411-421. |
| [5] | Rajendra K.Krishnaswamy .Analysis of ductile and brittle failures from creep rupture testing of high-density polyethylene (HDPE) pipes[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(25):11664-11672. |
| [6] | 李明,温茂萍,何强,庞海燕,敬世明.TATB基高聚物粘结炸药的蠕变特性研究[J].含能材料,2005(03):150-154. |
| [7] | Dean GD;Broughton W .A model for non-linear creep in polypropylene[J].Polymer Testing,2007(8):1068-1081. |
| [8] | 罗文波,安群力,杨挺青.非线性粘弹体的时间-温度-应力等效原理及其应用[J].固体力学学报,2001(03):219-224. |
| [9] | 王初红,罗文波,赵荣国,唐欣.应力对聚丙烯蠕变行为的时间-温度等效性的影响[J].湘潭大学自然科学学报,2006(04):31-34. |
| [10] | 穆霞英.蠕变力学[M].西安:西安交通大学出版社,1990 |
| [11] | 刘伟,高宗战,岳珠峰.MDYB-3有机玻璃疲劳性能温度效应研究[J].航空学报,2007(04):874-876. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%