对GH4169合金焊接接头在650℃下的疲劳裂纹扩展性能进行了测试和分析.结果表明,疲劳裂纹扩展速率、初始裂纹尺寸、裂纹容限和温度对焊接接头的疲劳裂纹扩展寿命都有影响.母材及焊缝的疲劳裂纹扩展速率和裂纹容限均有较大的差异.
The experimental study on fatigue crack growth of GH4169 superalloy has been carried out. The temperatures of fatigue crack growth tests was 650℃. The results show that the fatigue crack growth rate,initial crack length,critical crack and temperature all have an effect on fatigue crack growth of GH4169. The fatigue crack growth and critical crack of base metal and joints also have great difference.
参考文献
| [1] | S. A. Padula II;A. Shyam;R. O. Ritchie;W. W. Milligan .High frequency fatigue crack propagation behavior of a nickel-base turbine disk alloy[J].International Journal of Fatigue,1999(7):725-731. |
| [2] | 李树祺.GH169合金显微组织对合金裂纹扩展速率的影响[J].材料工程,1998(05):26. |
| [3] | 周建波,董建新,徐志超,谢锡善.GH761涡轮盘650℃疲劳/蠕变交互作用下的裂纹扩展速率[J].特殊钢,2002(03):19-20. |
| [4] | 何玉怀,李骋,刘绍伦,韩希鹏,苏彬.GH4169合金疲劳裂纹扩展性能的试验研究[J].燃气涡轮试验与研究,2004(04):5-8. |
| [5] | 霍立兴.焊接结构的断裂行为及评定[M].北京:机械工业出版社,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%