在800,850,900℃的温度条件下,对第二代单晶高温合金DD6的横向持久性能进行了研究.结果表明:与相同条件下的纵向即[001]取向持久性能相比,合金横向持久寿命低于纵向持久寿命.在相对较高温度下,合金横向与纵向的持久寿命在数值上相差较小;在相对较低温度下,合金横向持久寿命明显低于纵向.随着实验温度的升高,扩散蠕变作用增强,韧窝断裂的倾向增加,同时枝晶间和枝晶干变形均匀,横向持久性能相对提高而接近于纵向持久性能.垂直于应力轴的一次枝晶界和枝晶间区域的存在,是横向持久性能低于[001]取向的主要原因.
参考文献
[1] | DAVIS J R.Heat resistant materials-ASM specialty handbook[M].USA:ASM International,Materials Park,1997 |
[2] | SIMS C T;STOLOFF N S;HAGEL W C.Superalloys II[M].New York:wiley,1987 |
[3] | ALEXANDER EPISHIN;THOMAS LINK;BERNAR FEDELICH.Effects of segregation in nickel-base superalloys:dentritics stress[A].Warrendale,PA:TMS,2004:537-543. |
[4] | DAVID A WOODFORD.Creep strength and fracture resistance of directionally solidified GTD111[A].Warrendale,PA:TMS,1996:353-357. |
[5] | ZHU YAOXIAO;RADAVICH F JOHN;ZHENG ZHI.The development and long-time structural stability of a low segregation Hf free Superalloy-DZ125L[A].Warrendale,PA:TMS,2000:329-339. |
[6] | Q.Z. Chen;N. Jones;D.M. Knowles .The microstructures of base/modified RR2072 SX superalloys and their effects on creep properties at elevated temperatures[J].Acta materialia,2002(5):1095-1112. |
[7] | MACLACH D W;KNOWLES D M .Modelling and prediction of the stress rupture behaviour of single crystal superalloys[J].Materials Science and Engineering,2001,302 A:275-285. |
[8] | LEMAITRE J;CHABOCHE J L.Mechanics of Solid Materials[M].Cambridge:Cambridge University Press,1985 |
[9] | MARTIN HEILMAIER;MICHEL NAGANBE;FRANK E H.The effect of strain rate and temperature on the LCF behavior of the ODS nickel-base superallooy[A].Warrendale,PA:TMS,2000:593-600. |
[10] | YUE Z F;LU Z Z;ZHENG C Q .Fracture behavior of a nickel-base single crystal superalloy as predicted by the energy density criterion[J].Theoretical and Applied Fracture Mechanics,1997,26:89-104. |
[11] | MERRILL J M;WILCOX R C.Metallographic Characterization of Materials Behavior[M].United States:Charleston,South Carolina,1994 |
[12] | ALEXANDER EPISHIN;THOMAS LINK.Mechanisms of high temperature creep of nickel-base superallpys under low applied stress[A].Warrendale,PA:TMS,2004:137-144. |
[13] | ZHANG J X;MURAKUMO T;KOIZUMI Y et al.Slip geometry of dislocations related to cutting of the γ phase in a new generation single-crystal superalloy[J].Acta Materialia,2003,51:5073-5081. |
[14] | DYMEK S;DOLLAR M;IYER A.Effects of long range ordering,temperature and strain rate on deformation behavior of a Ni-Mo-Cr alloy[A].Warrendale,PA:TMS,1992:685-694. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%