选用牌号为YG6,YG6X,YT15和YS8四种硬质合金刀具材料,利用电阻炉对刀具材料加热保温,进行刀具材料的抗氧化性能实验.结果表明:氧化实验中,刀具材料表面的WC被部分氧化成WO3;Co元素被氧化成Co3O4,而刀具材料中的TiC非常稳定,在温度达到1300K时才发现其氧化产物TiO2;含有TiC的刀具材料比不含TiC的刀具材料具有更好的抗氧化性能,晶粒小的刀具材料比晶粒粗大的刀具材料有更好的抗氧化性能;四种刀具材料的高温抗氧化性能好坏顺序为:YS8>YT15>YG6X>YG6.
参考文献
| [1] | 邓建新;赵军.数控刀具材料选用手册[M].北京:机械工业出版社,2005 |
| [2] | EZUGWU E O;WANG Z M .Titanium alloys and their machinability-a review[J].Journal of Materials Processing Technology,1997,68(03):262-274. |
| [3] | A. Jawaid;C. H. Che-Haron;A. Abdullah .Tool wear characteristics in turning of titanium alloy Ti-6246[J].Journal of Materials Processing Technology,1999(0):329-334. |
| [4] | G. List;M. Nouari;D. Gehin;S. Gomez;J. P. Manaud;Y. Le Petitcorps;F. Girot .Wear behaviour of cemented carbide tools in dry machining of aluminium alloy[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(2):1177-1189. |
| [5] | Luigino Filice;Fabrizio Micari;Luca Settineri;Domenico Umbrello .Wear modelling in mild steel orthogonal cutting when using uncoated carbide tools[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2007(5/6):545-554. |
| [6] | P. Kindermann;P. Schlund .High-temperature fatigue of cemented carbides under cyclic loads[J].International Journal of Refractory Metals & Hard Materials,1999(1/3):55-68. |
| [7] | 刘战强,艾兴.高速切削刀具磨损表面形态研究[J].摩擦学学报,2002(06):468-471. |
| [8] | 龙震海,王西彬,刘志兵.高速铣削难加工材料时硬质合金刀具前刀面磨损机理及切削性能研究[J].摩擦学学报,2005(01):83-87. |
| [9] | 叶大伦;胡建华.实用无机物热力学数据手册[M].北京:冶金工业出版社,2002 |
| [10] | 肖诗纲.刀具材料及其合理选择[M].北京:机械工业出版社,1990 |
| [11] | 谭树松.有色金属材料学[M].北京:冶金工业出版社,1993 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%