采用化学共沉淀法制备了纳米Ni0.5Zn0.5CexFe2-xO4(x=0,0.005,0.01,0.015)铁氧体吸波材料,用AV3618型微波矢量网络分析仪测试了样品在8.2～12.5GHz范围内的微波吸收特性,实验结果表明:稀土元素铈的含量影响材料的吸波性能,当x=0.01时, 纳米Ni0.5Zn0.5CexFe2-xO4铁氧体的吸波性能最佳.对于Ni0.5Zn0.5Ce0.01Fe1.99O4铁氧体吸波材料,当涂层厚度为1mm时,在测试频段内有三个吸收峰,在8.8GHz处,其最大吸收衰减量为15.4dB,10 dB以上带宽达3.8GHz,适量掺杂稀土元素铈是提高镍锌铁氧体吸波材料性能的一种有效途径.
参考文献
| [1] | 邢丽英.隐身材料[M].北京:化学工业出版社,2004:172-176. |
| [2] | 徐坚,熊惟皓,曾爱香,王采芳.稀土元素在磁性吸波材料中的应用研究进展[J].稀土,2004(06):68-73. |
| [3] | 阮圣平,吴凤清,王永为,张力,乌日娜,宣丽.钡铁氧体纳米复合材料的制备及其微波吸收性能[J].物理化学学报,2003(03):275-277. |
| [4] | M. R. Meshram;Nawal K. Agrawal;Bharoti Sinha .Characterization of M-type barium hexagonal ferrite-based wide band microwave absorber[J].Journal of Magnetism and Magnetic Materials,2004(2/3):207-214. |
| [5] | Sileo EE.;Rotelo R.;Jacobo SE. .Nickel zinc ferrites prepared by the citrate precursor method[J].Physica, B. Condensed Matter,2002(1/4):257-260. |
| [6] | 李东风,孟哲,贾振斌,魏雨.化学共沉淀法制备纳米级软磁铁氧体研究进展[J].应用科技,2003(04):54-56. |
| [7] | 庄稼,陈学平,迟燕华,刘燕梅.纳米Ni0.5Zn0.5Fe2O4铁氧体的制备及电磁损耗特性研究[J].功能材料,2006(01):43-46. |
| [8] | Sung-Soo Kim;Dae-Hee Han .Microwave absorbing properties of sintered Ni-Zn ferrite[J].IEEE Transactions on Magnetics,1994(6):4554-4556. |
| [9] | 黄永杰.磁性材料[M].北京:电子工业出版社,1994:200-203. |
| [10] | 庄稼,迟燕华,石军宁,朱达川,涂铭旌.铈对纳米铁氧体粉末电磁学性质影响的研究[J].中国稀土学报,2002(04):324-326. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%