采用BNi82CrSiB钎料在1070℃/15min规范下对DD6单晶合金进行了真空钎焊实验研究.获得了致密完整的钎焊接头,钎料元素未向母材扩散.钎焊接头在750℃的抗拉强度为400 MPa左右,750℃/100h持久强度可达100MPa.钎焊接头的失效断裂源自焊缝中间的化合物相上,断口呈脆性断裂特征.
参考文献
| [1] | 《中国航空材料手册》编辑委员会.中国航空材料手册第2卷变形高温合金铸造高温合金[M].北京:中国标准出版社,2002 |
| [2] | 李嘉荣;钟振纲;唐定中 等.低成本第二代单晶高温合金DD6[J].金属学报,1999,35(z2):S266-S269. |
| [3] | LI J R;ZHONG Z G;TANG D Z.A low-cost second generation single crystal superalloy DD6[A].Warrendale,PA:The Minerals,Metals & Materials Society,2000:777-783. |
| [4] | BROOMFIELD R W.Development of brazing techniques for the joining of single crystal components[M].Cambridge:Cambridge University Press,2000:741-754. |
| [5] | MIGLIETTI W M;PENNEFATHER R C.Microstructure,mechanical properties and coatability of diffusion brazed CMSX-4 single crystal[A].Materials Park,Ohio:ASM International,1997:61-77. |
| [6] | NISHIMOTO K;SAIDA K;KIM D et al.Homogenization behavior of alloying elements during transient liquid phase bonding[J].Quarterly Journal of the Japan Welding Society,1997,15(03):509-514. |
| [7] | 李晓红,毛唯,郭万林,谢永慧.DD6单晶合金过渡液相扩散焊工艺[J].焊接学报,2005(04):51-54. |
| [8] | 张启运;庄鸿寿.钎焊手册[M].北京:机械工业出版社,1998 |
| [9] | GB 10859-1989.GB 10859-1989.镍基钎料[S]. |
| [10] | S. K. Tung;L. C. Lim;M. O. Lai .Solidification phenomena in nickel base brazes containing boron and silicon[J].Scripta materialia,1996(5):763-769. |
| [11] | 庄鸿寿;罗格夏特 E.高温钎焊[M].北京:国防工业出版社,1989 |
| [12] | 毛唯,何剑雄,叶雷,张学军,陈波.BNi82CrSiB钎料钎焊K403合金接头的性能[C].第十一次全国焊接会议论文集(第1册),2005:91-93. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%