利用熔体快淬和晶化处理方法制备了Pr2Fe14B/α-Fe纳米复合永磁材料.采用X射线衍射分析(XRD)、差热分析(DTA)、磁性测量(VSM)等方法对合金的晶化行为和磁性能进行研究.结果发现对于Pr2Fe14B/α-Fe熔体快淬永磁粉末,α-Fe相析出温度对材料升温速率敏感,可通过提高升温速率尽量使α-Fe和Pr2Fe14B两相的析出温度接近,但难以找到一个温度使两相同时大量析出.(Pr8.2Fe86.1B5.7)0.99Zr1淬态合金在963K时,会生成亚稳相Pr2Fe23B3,使磁性能恶化,延长晶化热处理时间或增高晶化热处理温度均可使亚稳相分解.合金在合适的条件下热处理后,材料磁性能较淬态样品有明显提高.
参考文献
| [1] | COEHOORN R;DE MOOIJ D B;DE WAARD C .Meltspun permanent magnet materials containing Fe3B as the main phase[J].Journal of Magnetism and Magnetic Materials,1989,80:101-104. |
| [2] | Kneller E.F.;Hawig R. .The exchange-spring magnet: a new material principle for permanent magnets[J].IEEE Transactions on Magnetics,1991(4):3588-3560. |
| [3] | 庞利佳,乔祎,陈菊芳,孙光飞,祁毓俊,胡权霞.纳米复合永磁材料晶粒择优取向的研究[J].中国稀土学报,2004(06):773-777. |
| [4] | S. Hirosawa;Y. Shigemoto;T. Miyoshi;H. Kanekiyo .Direct formation of Fe_3B/Nd_2Fe_(14)B nanocomposite permanent magnets in rapid solidification[J].Scripta materialia,2003(7):839-844. |
| [5] | 庞利佳,孙光飞,陈菊芳,喻晓军,黎文安,张锦标.纳米晶复合永磁材料各向异性的研究进展[J].金属功能材料,2005(04):20-24. |
| [6] | Y.Q. Wu;D.H. Ping;B.S. Murty .Influence of heating rate on the microstructure and magnetic properties of Fe_3B/Nd_2Fe_(14)B nanocomposite magnets[J].Scripta materialia,2001(3):355-362. |
| [7] | Effect of additions on the crystallization process, structure, and magnetic properties of (NdPr)-Fe-B amorphous ribbons[J].Journal of Applied Physics,2003(10):8149-8151. |
| [8] | 王佐诚,乔祎.纳米复合Pr2（FeZr）14B/α-Fe永磁合金[J].金属功能材料,1998(02):65. |
| [9] | YANG S;LIS D;LIU X S et al.Exchange coupled Nd2Fe14B/α-Fe nanocomposite magnets with fine α-Fe grains obtained by low wheel speed spinning[J].Journal of Alloys and Compounds,2002,343:217-222. |
| [10] | GONG W;MA B M .Comparison on the magnetic and structural properties of Sm(Co0.67-xFe0.25Cu0.06Zr0.02Cx)8.0,where x = 0-0.15,melt spun ribbons and cast alloys[J].Journal of Applied Physics,1999,85(08):4657-4659. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%