采用磷酸阳极化方法对胶接修理铝合金裂纹板的粘接表面进行了处理,并用单向碳纤维/环氧复合材料补片对铝合金进行了修补.测试了阳极化铝合金的粘接性能、修补结构的静态力学性能和疲劳性能,考察了粘接表面的阳极化处理对修补结构的静态力学性能和疲劳性能的影响.结果表明,磷酸阳极化在铝合金表面形成多孔膜,复合材料补片修补胶接时胶粘剂能渗透进入阳极化铝合金表面的多孔膜,在粘接界面上形成一层过渡层,该过渡层的形成能有效提高其与复合材料的粘接性能,其粘接副的拉剪强度提高了104%;铝合金裂纹板胶接修理前的粘接表面的阳极化处理能大幅度地提高修复结构的静态强度和疲劳寿命,当用单向碳纤维/环氧复合材料补片单面修补时,修补结构的破坏强度为418.13MPa,恢复到完好板的93.42%;修补结构的疲劳寿命相对裂纹板延长了1.42倍,比未阳极化的修补板的疲劳寿命增加了27.59%.修补前的阳极化处理也使修补结构在一定周次疲劳后的剩余强度有所提高.
参考文献
| [1] | 陈绍杰.复合材料结构修理指南[M].北京:航空工业出版社,2001 |
| [2] | BAKER A A.Bonded Repair of Aircraft Structure[M].Dordrecht,Netherlands:Martinus Nijhoff Publishers,1988 |
| [3] | 徐建新 .损伤金属结构的复合材料胶接修补技术研究[D].南京航空航天大学,1996. |
| [4] | 孙宏涛 .复合材料胶接修补止裂技术的理论及试验研究[D].西安:西北工业大学,1998. |
| [5] | BAKER A A .Fiber composite repair of cracked metallic aircraft components:practical and basic aspects[J].Composites,1987,18(04):293-307. |
| [6] | BAKER A A .Reinforcement of the F-111 wing pivot fitting with a born/epoxy doubler system materials engineering aspects[J].Composites,1993,24(06):511-521. |
| [7] | 陈绍杰.用复合材料技术修理金属飞机结构[J].航空制造技术,1996(09):33-34. |
| [8] | 陈绍杰.飞机复合材料结构修理--世纪之交复合材料的现状与发展[M].长沙:湖南科学技术出版社,1998:42-47. |
| [9] | 复合材料补片胶接修理技术的研究进展[J].航空学报,1999(04):381. |
| [10] | 赵云峰.表面处理对硅橡胶胶粘剂胶接性能的影响[J].化学与粘合,2001(02):49-51. |
| [11] | 陈明安,张新明,蒋志军,傅杰兴,雷秋玲.铝及铝合金表面处理后的表面特征和粘接特性[J].化学与粘合,2001(06):262-264,267. |
| [12] | LUNDER O;OLSEN B;NISANCIOGLU .Pre-treatment of AA6060 aluminum alloy for adhesive bonding[J].International Journal of Adhesion and Adhesives,2002,22:143-150. |
| [13] | ASTRID B;FABRICE L;JOHN W .Anodising as pre-treatment for structural bonding[J].International Journal of Adhesion and Adhesives,2003,23:401-412. |
| [14] | Joseph H.Osborne;Kay Y.Blohowiak;S.Ray Taylor;Chad Hunter;Gordon Bierwagon;Brendon Carlson;Dan Bernard;Air force research laboratory nonmetallic mateirals directorate WPAFB OH 45433-7750 USA;Michael S. Donley .Testing and evaluation of nonchromated coating systems for aerospace applications[J].Progress in Organic Coatings: An International Review Journal,2001(4):217-225. |
| [15] | ASTM D 1002-01.ASTM D 1002-01.Standard Test Method for Apparent Shear Strength of Single-Lap-Joint Adhesively Bonded Metal Specimens by Tension Loading (Metal-to-Metal)[S].Pennsylvania,USA:Annual Book of ASTM Standards,2001. |
| [16] | 曾华梁;杨家昌.电解和化学转化膜[M].北京:中国轻工业出版社,1987 |
| [17] | 陈篪;蔡其巩;王仁智.工程断裂力学[M].北京:国防工业出版社,1978 |
| [18] | WANG Q Y;PIDAPARTI R M .Static characteristics and fatigue behavior of composite repaired aluminum plates[J].Computers and Structures,2002,56:151-155. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%