镍基单晶高温合金是高推重比发动机涡轮叶片的关键材料.综述了镍基单晶高温合金的反常屈服行为,并讨论了导致产生这种反常屈服行为的变形机制及这些变形机制的发展过程.
参考文献
| [1] | S X Li;E G Fllison;D J Smith .[J].Journal of Strain Analysis,1994,29(02):147-153. |
| [2] | S X Li;D J Smith .[J].Materials Science and Technology,1995,11:1253-1260. |
| [3] | S S K Gunturi;D W MacLachlan .[J].Materials Science and Engineering,2000,A289:289-297. |
| [4] | R Chieragatti;L Remy .[J].Materials Science and Engineering,1991,A141:1-9. |
| [5] | J S Crompton;J W Marton .[J].Materials Science and Engineering,1984,64:37-43. |
| [6] | S M Copley;B H Kear;G M Powe .[J].Materials Science and Engineering,1972,10:87-93. |
| [7] | W W Milligan;S D Antolovich .[J].Metallurgical and Materials Transactions,1987,18A:85-95. |
| [8] | D P Pope;S S Ezz .[J].International Metals Reviews,1984,29(03):136-167. |
| [9] | D M Shah;D N Duhl.[A].Warrendale:PA,1984:105-114. |
| [10] | R G Davies;T L Johnston.[M].Ordered Alloy,1970:447. |
| [11] | D M Shah;D N Duhl .[J].Journal of Metals,1981,33(12):24. |
| [12] | S M Copley;B H Kear .[J].Transactions AIME,1967,239:984. |
| [13] | D A Finn .[J].Transactions AIME,1960,218:145. |
| [14] | B H Kear;H G F Wilsdorf .[J].Transactions AIME,1962,224:382. |
| [15] | P H Thornton;R G Davies;T L Johnston .[J].Metallurgical and Materials Transactions,1970,1:207. |
| [16] | S Takiuchi;E Kuramoto .[J].Acta Materialia,1973,21:1415. |
| [17] | C Lall;S Chin;D P Pope .[J].Metallurgical and Materials Transactions,1979,10A:1323. |
| [18] | V Paidar;D P Pope;V Vitek .[J].Acta Materialia,1984,32:435-448. |
| [19] | B H Dear;B J Piearcey .[J].Transactions AIME,1987,279:1209. |
| [20] | B H Kear;A F Giamei;J M Silcock;R K Ham .[J].Scripta Metallurgica et Materialia,1969,3:123. |
| [21] | P Caron;T Khan .[J].Philosophical Magazine,1988,57A:859. |
| [22] | M Condat;B Decamps .[J].Scripta Metallurgica et Materialia,1987,21:607-609. |
| [23] | W W Milligan;S D Antolovich .[J].Metallurgical and Materials Transactions,1991,22A:2309-2318. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%