真空自耗电弧炉熔炼方法生产的钛合金锭可能存在许多缺陷,如难熔金属夹杂、间隙元素偏析、合金元素偏析所致的组织缺陷、反常的α相形态等组织缺陷以及化学成分的偏析.其中宏观偏析是必然存在且最难解决的一个,本文对典型Ti-2.5Cu钛合金进行了微区成分分析和宏观成分分析,得出了合金元素宏观和微观偏析的规律,并探讨了引起宏观偏析的微观原因.
参考文献
| [1] | 王金友;葛志明;周彦邦.航空用钛合金[M].上海:上海科学技术出版社,1985 |
| [2] | C H Eentrekin;H R Harker.Recent development in electron beam hearth refining[A].France,1998:615-619. |
| [3] | M Ostheimer;S R Seagle.Utilization of electron beam melting in the production of defect free Ti-6Al-4V ingots[A].France,1998:579-582. |
| [4] | 宁兴龙,王国宏.钛合金铸锭的凝壳-自耗电极熔炼[J].钛工业进展,2000(01):41-45. |
| [5] | 王镐;高颀;李奔放 .熔化电流对Ti-811合金铸锭化学成分的影响[J].金属学报,1999,35(z1):534-537. |
| [6] | A Jardy;S Hans;D Ablitzer.A Theoretical atudy of the influence of process parameters on the macrosegregation in vacuum arc remelted βCez ingots[A].:1507-1512. |
| [7] | X Cai;Y Dou;P Li.The control of the solidifying segregation of Ti-2. 5Cu alloy[A].France,1998:637-641. |
| [8] | P A Blenkinsop;D F Neal.High temperature alloys-The metallurgical understanding,development and achievements of conventional alloys[A].,1993:1861-1868. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%