介绍了聚环氧乙烷(PEO)/LixMoO3纳米复合材料的制备工艺过程。X-射线衍射、示差扫描量热分析的结果表明,PEO大分子插入到LixMoO3片层间,形成纳米复合材料。此外,PEO插层LixMoO3后,材料的电学性能得到改善。
PEO/LixMoO3 nanocomposite was prepared by solution intercalationmethod. Powde rX-ray diffraction and differential scanning calorimetry show that PEO chains are intercalated into LixMoO3 galleries. Electrochemical Property of LixMo O3 is improved after PEO intercalation.
参考文献
[1] | 宋国君;舒文艺 .[J].材料导报,1996,2(04):57-60. |
[2] | C R Kannewurf;M G Kanatzidis .[J].CHEMISTRY OF MATERIALS,1991,3(06):992-994. |
[3] | L Wang;J Schindler;J Albritton .[J].Chemistry of Materials,1995,7:1753-1755. |
[4] | L F Nazar;Z Zhang;D Zinkweg .[J].Journal of the American Chemical Society,1992,114:6239-6240. |
[5] | R Bissessur;D C DeGroot.[J].Journal of the Chemical Society,Chemical Communications,1993:687-689. |
[6] | 杨兰生;单忠强;邹建梅 .[J].天津大学学报,1995,28(04):503-508. |
[7] | G G Hammes;P B Roberts .[J].Journal of the American Chemical Society,1968,90:7119-7124. |
[8] | D Thomas;E Mclarron .[J].Materials Research Bulletin,1986,21:945-960. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%