扫描电镜下采用动态拉伸法,原位观察SiCw/MB15复合材料在动态受载条件下裂纹形成、扩展至断裂的全过程,并对断口进行了分析。结果表明,裂纹主要在折断的晶须处萌生,在主裂纹前端应力集中区内长大、连结,在与主应力垂直方向上形成宏观裂纹。

The nucleation, propagation of cracks to fracture of SiCw/MB15composites were observed with tensile loading under SEM. It is discovered that cracks mainly nucleate at clearance between broken whiskers. The whole process of crack formation is that micro-cracks propagated and linked each other in the stress concentration zone of the main crack tip, then combined in the perpendicular direction of main stress to form a macro-crack.