在保持其它合金元素含量基本不变的情况下,分别加入2.2%、3.2%和4.2%的Re浇注单晶高温合金试块,研究了Re含量对单晶高温合金拉伸强度和蠕变断裂寿命等的影响.结果表明:随Re含量增加,649℃条件下的拉伸强度下降但塑性升高;982℃/248.2MPa、1038℃/206.8MPa及1070℃/176.8MPa条件下的蠕变断裂寿命显著提高而塑性有所降低;在相同的试验条件下,随合金的Re含量增加,在蠕变断裂寿命提高的同时,筏排组织变大.
参考文献
| [1] | W S Walston;K S O Hara;E W Eoss;R D Kissinger et al.Superalloys 1996[J].TMS,1996,27 |
| [2] | G L Erickson;R D Kissinger.Superalloys 1998[M].TMS,1996:35. |
| [3] | 陈荣章.单晶高温合金发展现状[J].材料工程,1995(08):3. |
| [4] | G L Erickson.The Development of CMSX-10,A Third Generation SX Casting Superalloy[A].Kyongju,Korea,1995 |
| [5] | 李嘉荣.铼（Re）在单晶高温合金中的作用[J].材料工程,1997(08):3. |
| [6] | A F Giamei;D L Auton .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1997,16A(11) |
| [7] | D Blavette;P Caron;T Khan;D N Duhl.Superalloys 1988[M].TMS,1988:305. |
| [8] | W S Walston;J C Schaeffer;W H Murphy;R D Kissinger.Superalloys 1996[M].TMS,1996:9. |
| [9] | R N Nabarro .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1996,27A(03):513. |
| [10] | C T Sims;N S Stoloff;赵杰.高温合金[M].大连:大连理工大学出版社,1992 |
| [11] | W Schneider;J Hammer;H Mughrabi;S D Antolovich.Superalloys 1992[M].TMS,1992:589. |
| [12] | J Hammer .[D].Ph D Thesis,University Erlangen-Nrnberg,Nrnberg,Germany,1990. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%