提出了一种化学去毛刺技术,去毛刺液的组成(质量分数)为70%磷酸+12%草酸+18%水,去毛刺时控制溶液温度在45～60℃、时间为10～45 min即可.运用体视显微镜、扫描电子显微镜、X-ray衍射仪和维氏硬度计等手段考察了此化学去毛刺技术处理有色金属制精密零件的效果,认为此化学去毛刺技术可以达到精度要求、技术要求和质量要求,不改变零件的性能,且具有一定的光亮作用.
参考文献
| [1] | 安军,李洪友,周锦进.脉冲电化学去毛刺工艺[J].工具技术,2002(12):42-44. |
| [2] | 王贵成,陈镇宇,裴宏杰,朱云明.金属切削毛刺专家知识系统的开发[J].中国制造业信息化,2004(10):116-118. |
| [3] | Sung-Lim Ko;Jing-Koo Lee .Analysis of burr formation in drilling with a new-concept drill[J].Journal of Materials Processing Technology,2001(1/3):392-398. |
| [4] | Lin Tasann-rong .Experimental Study of Burr Formation and Tool Chipping in the Face Milling of Stainless Steel[J].Journal of Materials Processing Technology,1999,108(01):12-20. |
| [5] | Ko S L;Dornfeld D A.Study on Burr Formation Mechanism[A].,1998:271-282. |
| [6] | Hashimura M;UeDa K;Dornfeld D et al.Analysis of Three dimensional Burr Formation in Oblique Cutting[J].Annals of the CIRP,1995,44(01):27-30. |
| [7] | Sangkee Min;Jinsoo Kim;David A. Dornfeld .Development of a drilling burr control chart for low alloy steel, AISI 4118[J].Journal of Materials Processing Technology,2001(1/3):4-9. |
| [8] | 皮启德.热能去毛刺锌合金钝化件的前处理[J].材料保护,2000(08):22. |
| [9] | 姜黄海.热能去毛刺技术[J].航天制造技术,2002(01):21-24. |
| [10] | Yeo S H;Bryan B K A Ngoi;Chua L Y .Ultrasonic Deburring[J].Int J Adv Manuf Tecnol,1997,13:333-341. |
| [11] | 李富长.电化学去毛刺技术在航空产品中的应用[J].航空精密制造技术,2004(01):16-17. |
| [12] | 丁建刚,洪若瑜,王廖沙.钢基体材料化学去毛刺工艺的研究进展[J].材料保护,2007(07):56-58. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%