以正硅酸乙酯（TEOS）为硅源，无水乙醇为溶剂，硝酸为催化剂，氨水为凝胶剂，经溶胶-凝胶过程制备块状湿凝胶。再以三甲基氯硅烷（TMC S ）为疏水改性剂，3-氨丙基三羟基硅烷为亲水改性剂对制备的湿凝胶进行改性处理，最后经超临界CO2干燥得到块体SiO2气凝胶。考察了亲水改性剂加入量分别为0、0．15、0．75、1．5、2．70 mL时对块体SiO2气凝胶亲水性的影响，并通过扫描电子显微镜（SEM）、接触角、吸水率、红外光谱（FT-IR）等对气凝胶进行表征。结果表明：所得气凝胶块体具有纳米多孔结构，内部疏水（最大接触角可达123°），表面亲水，试样亲水性随亲水剂用量的增加而增大；同一试样亲水性存在一定的梯度变化，亲水性由内到外逐渐增强。
Wet silica gel monoliths were prepared by sol-gel process using tetraethoxysilane (TEOS)as sil-ica source,absolute ethyl alcohol as solvent,nitrating acid as catalyzer,and ammonia as gelata.Then the wet gels were modified by trimethyl methylchlorosilane(TMCS)and 3-ammonia three hydroxyl propyl si-lane as hydrophobic modifier and hydrophilic modifier,respectively.After CO2 supercritical drying,silica aerogels were obtained.The impacts on hydrophilicity of silica aerogels with hydrophilic modifier dosages of 0,0.15,0.75,1.05 and 2.70 mL were investigated,respectively.Silica aerogels were characterized by scanning electron microscope (SEM),contact angle,water absorption rate,and infrared spectroscopy (FT-IR).The results show that:the prepared silica aerogels have nano-porous structures;the inner aerogel is hydrophobic (the maximum contact angle can reach 123°)and the surface is hydrophilic,the hydrophilicity of silica aerogels increases with the dosage of hydrophilic modifier increasing.There is a certain gradient change of hydrophilicity in the same specimen and the hydrophilicity increases from inner to outer.
参考文献
| [1] | Bhagat SD;Rao AV .Surface chemical modification of TEOS based silica aerogels synthesized by two step (acid-base) sol-gel process[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(12):4289-4297. |
| [2] | Schmidt M.;Schwertfeger F. .Applications for silica aerogel products[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):364-368. |
| [3] | 何方,熊先文,吴菊英,黄渝鸿,张瑞珠,邹文俊,彭进,马秋花,朱贺,李荣春.SiO2气凝胶微球的雾化制备及表征[J].功能材料,2013(01):143-146. |
| [4] | Hegde ND;Rao AV .Organic modification of TEOS based silica aerogels using hexadecyltrimethoxysilane as a hydrophobic reagent[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(3):1566-1572. |
| [5] | Rao A V;Pajonk G M;Parvathy N N .Effect of solvents and catalysts on monolithicity and physical properties of silica aerogels[J].J Ma-ter Sci,1994,29(07):1807-1817. |
| [6] | Sung-Woo Hwang;Tae-Youn Kim;Sang-Hoon Hyun .Effect of surface modification conditions on the synthesis of mesoporous crack-free silica aerogel monoliths from waterglass via ambient-drying[J].Microporous and mesoporous materials: The offical journal of the International Zeolite Association,2010(1/3):295-302. |
| [7] | Al-Oweini, R;Ei-Rassy, H .Synthesis and characterization by FTIR spectroscopy of silica aerogels prepared using several Si(OR)(4) and R '' Si(OR ')(3) precursors[J].Journal of Molecular Structure,2009(1/3):140-145. |
| [8] | Catherine A. Morris;Michele L. Anderson;Rhonda M. Stroud .Silica Sol as a Nanoglue: Flexible Synthesis of Composite Aerogels[J].Science,1999(5414):622-624. |
| [9] | Yokogawa H;Yokoyama M .Hydrophobic silica aerogels[J].JOURNAL OF NON-CRYSTALLINE SOLIDS,1995,186(02):23-29. |
| [10] | 汪武,陈建,黄昆.常压制备疏水性二氧化硅气凝胶[J].无机盐工业,2011(05):43-45. |
| [11] | Ayse Merif Kartal;Can Erkey .Surface modification of silica aerogels by hexamethyldisilazane-carbon dioxide mixtures and their phase behavior[J].The Journal of Supercritical Fluids,2010(1/3):115-120. |
| [12] | Duan, Y.;Jana, S.C.;Lama, B.;Espe, M.P. .Reinforcement of silica aerogels using silane-end-capped polyurethanes[J].Langmuir: The ACS Journal of Surfaces and Colloids,2013(20):6156-6165. |
| [13] | Yang HF.;Shi QH.;Tian BZ.;Xie SH.;Zhang FQ.;Yan Y.;Tu B.;Zhao DY. .A fast way for preparing crack-free mesostructured silica monolith[J].Chemistry of Materials,2003(2):536-541. |
| [14] | Sarawade, P.B.;Kim, J.-K.;Hilonga, A.;Quang, D.V.;Jeon, S.J.;Kim, H.T. .Synthesis of sodium silicate-based hydrophilic silica aerogel beads with superior properties: Effect of heat-treatment[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2011(10):2156-2162. |
| [15] | Wagh P B;Ingale S V .Comparison of some physico-chemical prop-erties of hydrophilic and hydrophobic silica aerogels[J].CERAMICS INTERNATIONAL,2002,28(01):43-50. |
| [16] | 代亚平,吴平霄.3-氨丙基三乙氧基硅烷改性蒙脱石的表征及其对Sr（Ⅱ）的吸附研究[J].环境科学学报,2012(10):2402-2407. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%