以天然硅灰石、滑石和石英砂为主要原料,以稀土氧化物作为添加剂,采用熔融-喷吹法制备了CaO-MgO-SiO2系生物可溶性陶瓷纤维.对熔体的黏度以及纤维的生物可溶性和高温析晶行为进行了研究.结果表明:添加稀土氧化物可以大大拓宽熔体成纤操作的温度范围;稀土氧化物的引入导致CaO-MgO-SiO2系生物可溶性陶瓷纤维在人体肺液中的溶解速率有所下降,但没有改变其生物可溶属性;引入稀土氧化物加强了CaO-MgO-SiO2系生物可溶性陶瓷纤维的网络结构,抑制了其高温析晶行为.
参考文献
[1] | Oberdǒrster G .Determinants of the pathogenicity of man-made vitreous fibers (MMVF)[J].International Archives of Occupational and Environmental Health,2000,73(01):60-68. |
[2] | 周立鸣,李平.生物可溶矿物纤维[J].新型建筑材料,2002(12):23-26. |
[3] | McConnell E E .A science-based paradigm for the classification of synthetic vitreous fibers[J].Regulatory Toxicology and Pharmacology,2000,32(14):14-21. |
[4] | Moore MartinA;Boymel PaulM;Maxim LDaniel;Turim Jay .Categorization and nomenclature of vitreous silicate wools.[J].Regulatory Toxicology and Pharmacology: RTP,2002(1):1-13. |
[5] | 王玺堂,张保国,王周福,刘浩,张少伟.CaO-MgO-SiO2系生物可溶性陶瓷纤维的研究[J].武汉科技大学学报(自然科学版),2008(03):238-241. |
[6] | 刘浩,王玺堂,王周福,张保国.二氧化钛包覆对钙镁硅系陶瓷纤维晶化行为的影响[J].武汉科技大学学报(自然科学版),2009(02):170-172,177. |
[7] | 刘缙,魏平,蔡序珩.硅灰石在玻璃生产中的应用研究[J].玻璃与搪瓷,2006(05):19-22. |
[8] | 张保国,王玺堂,刘浩.Y2O3对CaO-MgO-SiO2系可溶性陶瓷纤维析晶性能的影响[J].材料导报,2008(Z2):382-384. |
[9] | 李宏,郑勇,程金树.稀土掺杂对LAS系统微晶玻璃粘度的影响[J].武汉理工大学学报,2007(07):10-12,17. |
[10] | 林宗寿.无机非金属材料工艺学[M].武汉:武汉理工大学出版社,2006:262-263. |
[11] | 何世英.安瓿脱片问题的探讨[J].玻璃与搪瓷,1984(05):9. |
[12] | 崔之开.陶瓷纤维[M].北京:化学工业出版社,2003:8-9. |
[13] | Roy B N .Infrared spectroscopy of lead and alkaline-earth aluminosilicate glasses[J].Journal of the American Ceramic Society,1990,73(04):846-855. |
[14] | Merzbacher C L;White W B .The structure of alkaline earth aluminosilicate glasses as determined by vibrational spectroscopy[J].Journal of Non-Crystalline Solids,1991,131(01):18-34. |
[15] | M.Sroda;Cz.Paluszkiewicz .The structural role of alkaline earth ions in oxyfluoride aluminosilicate glasses-Infrared spectroscopy study[J].Vibrational Spectroscopy: An International Journal devoted to Applications of Infrared and Raman Spectroscopy,2008(2):246-250. |
[16] | Lange P .Evidence for disorder-induced vibrational mode coupling in thin amorphous SiO2 films[J].Journal of Applied Physics,1989,66(01):201-204. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%