采用光学显微镜、扫描电子显微镜、能谱仪、波谱仪和X射线衍射仪研究了熔铸α,β-Al2O3制品的显微结构,取自铸块表面向内100 mm厚度的样品分4段检验,表征了晶体形貌特征.结果发现:由于不同段带冷却速率的差异,致使主晶相仅α-Al2O3和β-Al2O3O的结晶形态呈现变异,显微结构明显不同,并且α-Al2O3和β-Al2O3在不同段带内的含量也不尽相同,由表面往里α-Al2O3的含量依次增加;以波谱仪测定了各段带β-Al2O3的组成,基本上属于n(Na2O):n(Al2O3)=1:(11～12)型的β-Al2O3组成范围;初晶相刚玉呈现包晶反应的典型形貌,而β-Al2O3结晶达毫米级柱状晶体,解理十分完全,解理面平直,间距为50-100μm;α-Al2O3和β-Al2O3晶体之间有一定量的气孔和结合相,结合相为霞石固溶体,其体积分数为2%～3%.
参考文献
| [1] | Baumann H N;Turner A A .Use of cast alumina refractories in glass industry[J].Journal of the American Ceramic Society,1940,23(11):334-338. |
| [2] | Baumann H N .Petrology of fused cast high alumina refractories[J].Bull Am Ceram Soe,1956,35(09):358-360. |
| [3] | Cooper A R .A critical completion of ceramic forming method:4,melt forming processes[J].Bull Am Ceram Soe,1965,44(01):1-8. |
| [4] | Sandmeyer K H;Miller W A .A fused cast alumina refractory[J].Bull Am Ceram Soc,1965,44(07):541-544. |
| [5] | 张玮;蒋齐安;邓延钦.熔铸α,β--Al2O3耐火材料及其在玻璃熔窑中的应用[J].耐火材料,1983(04):21-24. |
| [6] | 毛利民.熔铸α,β--Al2O3砖的结构与性能研究[J].中国建材科技,1999(03):32-34. |
| [7] | Carroll A F;Thornburg K S;Staten W T .Inhomgeneities in fusedeast alumina[J].JOURNAL OF THE CANADIAN CERAMIC SOCIETY,1982,51:43-46. |
| [8] | Hitchcock D C;Dejonghe L C .Fracture toughness anisotmpy of sodium 13-alumina[J].Journal of the American Ceramic Society,1983,66(I1):204-205. |
| [9] | Rolin M;Thanh P H.Les digrammes de phases des m～langes ne reagissant pas avec le molydene,1 le liquids du system aluminate de sodium -alumina[J].Rev Heutes Temper Et Refract,1965(02):175-185. |
| [10] | DeVries R C;ROTH W L .Critical evaluation of the literature data on beta alumina and related phases:I phase equilibria and characterization of beta alumina phase[J].Journal of the American Ceramic Society,1969,52(07):364-369. |
| [11] | Felsche J .The alkali problem in the crystal structure of beta alumina[J].Zeitschrift Far Kristallograpie,1968,127:94-100. |
| [12] | Li Xiangting;Guo Zhukun .A method for detecting mobile cation species and studying ion transport in solids[J].Solid State lonies,1990,40 -41(01):236-238. |
| [13] | 李香庭;郭祝岜 .钠与β-氧化铝陶瓷氧化物组分(包括氧化物杂质)之间的还原反应的热力学探讨[J].硅酸盐学报,1979,7(02):164-167. |
| [14] | 郭祝崑;李香庭 .金属钠在β-氧化铝陶瓷内的电解沉积现象[J].硅酸盐学报,1979,7(03):271-274. |
| [15] | 陈宗璋;杨进全;王昌贵 等.关于β-Al2O3固体电解质中钠沉积现象的研究[J].硅酸盐学报,1983,11(04):459-468. |
| [16] | 王佩玲;李香庭;陆昌伟.现代无机材料组成与结构表征[M].北京:高等教育出版社,2006:386-496. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%