采用中频炉的实验室模拟试验(试验条件:钢液温度1 600 ℃, 浸入时间30 min,气氛分别为空气和真空)和通过对用后耐火材料的显微结构分析,研究了钢液对3种连铸用含碳耐火材料(Al2O3-C、MgO-C和ZrO2-C)的侵蚀作用.结果表明,脱碳层的形成及钢液中夹杂物与脱碳层中耐火氧化物的反应是材料蚀损的主要原因.因此,在含碳耐火材料接触钢液的表面形成致密耐火层,能有效抑制钢液对连铸用含碳耐火材料的侵蚀.
参考文献
| [1] | Mukai K;Toguri J M;Stubina N M et al.A mechanism for local corrosion of immersion nozzle[J].ISIJ International,1989,29(06):469-476. |
| [2] | A.F.Dick;X.Yu .Attack of Submerged Entry Nozzles by Mould Flux and Dissolution of Refractory Oxides in the Flux[J].ISIJ International,1997(2):102-108. |
| [3] | W. L. da Costa Reis;S. N. Silva;J. A. Varela;E. Longo .Corrosion of the Immersion Nozzle during Steel Continuous Casting[J].Interceram: International Journal for Bricks, Structural Clay Products, Refractories, Pottery, Fine Ceramics, Abrasives and Special Ceramics,1998(2):88-96. |
| [4] | Joon Hyuk hong;Sung Man Kim .Slagline wear of graphite-bonded zirconia SENs[J].American Ceramic Society of Bulletin,1997,76(05):75-78. |
| [5] | Thomas Deinet;Olaf Krause;Jurgen Potschke.Studies on the wear of submerged entry nozzles[A].,2004:38-41. |
| [6] | 野村修;内田茂树 .Decarbonization Phenomena of Graphite Containing Refractories Caused by Molten Steel[J].品川技報,1998(41):25-36. |
| [7] | Osamu NOMURA;Shigeki UCHIDA;Wei LIN .Microstructure of Spinel SEN Used for Casting High-oxygen, Calcium-treated, Free-cutting and High-manganese Steels[J].品川技報,2001(44):47-56. |
| [8] | Takeshi Izaiku;Wei Lin;Shigeki Uchida et al.Development of a SEN for casting high oxygen steel[J].Journal of the Technical Association of Refractories,2002,22(04):383-385. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%