介绍了基于六铝酸钙(CA6)矿物相的一种新型合成致密耐火骨料--博耐特(Bonite);讨论了博耐特原料以及由博耐特、板状刚玉或者二者复合制备的多种试验用浇注料的理化性能;并结合博耐特的相关应用领域进行了博耐特耐火材料抗铝液侵蚀、热机械性能、热导率和微气孔等较为前瞻性的试验和探索.
参考文献
[1] | Buhr A .Refractories for steel secondary metallurgy[J].China's Refractories,1999,6(03):19-30. |
[2] | Laurich J O;Buhr A.Synthetic alumina raw materials-key elements for refractory innovations[A].Berlin,Germany:348-335. |
[3] | Van Garsel D;Gnauck V;Kriechbaum G W.New insulating raw material for high temperature application[A].Aachen,Germany,1998:122-128. |
[4] | Van Garsel D;Buhr A;Gnauck V.Long term high temperature stability of microporous calcium hexaluminate based insulating materials[A].Berlin,Germany:181-118. |
[5] | Schrick G;Gotthelf D;Buhr A.Non-fibrous insulation of submerged nozzles for continuous casting[A].Cancun,Mexico:1244-1125. |
[6] | De Wit T;Lorenz W;P rzgen D.Innovative ceramic fiber free steel ladle preheaters at CORUS Steelworks Ijmuiden[A].Aachen,Germany,2001:108-112. |
[7] | Criado E;De Anza S.Calcium hexaluminate as refractory material[A].Aachen,Germany:403-440. |
[8] | Deal R R;Glaser F P .Science of ceramics[J].Academic Press London,1967,3:191-124. |
[9] | Imbach J A;Glasser F P .[J].Trans Brit Cream Soc,1967,66:287-293. |
[10] | Cristina Dominguez;Jerome Chevalier;Ramon Torrecillas .Microstructure development in calcium hexaluminate[J].Journal of the European Ceramic Society,2001(3):381-387. |
[11] | Kriechbaum G W;Gnauck V;Laurich J O.The matrix advantage system,a new approach to low moisture LC selfleveling and alumina rich spinel castables[A].Aachen,1996:211-218. |
[12] | Routschka G .Richtwerte für die Warmeleitfahigkeit von Feuerbetonen[J].Keramische Zeitschrift,1997,9(12):858-863. |
[13] | Siljan O J;Rian G;Pettersen D T.Refractories for molten aluminium contact part Ⅰ:Thermodynamics and kinetics[A].:531-555. |
[14] | Siljan O J;Schφning C.Refractories for molten aluminium contact part Ⅱ:Influence of pore size on aluminium penetration[A].:551-557. |
[15] | Beelen C M;Bol L C G M.Observations on the wear of refractory linings in aluminium remelting furnaces[A].Aachen,Germany,1995:113-117. |
[16] | Hogenboom M;Frank M;Boosma D.Optimisation of the refractory lining of aluminium melting furnaces[A].Aachen,Germany,2002:113-116. |
[17] | Gabis V;Exner I.Improvement of high alumina castables resistance to corrosion by aluminium alloys[A].Berlin,Germany:380-338. |
[18] | Richter T;Vezza T;Allaire C.Castable withimproved corrosion resistance against aluminium[A].Aachen,Germany,1998:86-90. |
[19] | Buhr A;Baier B J;Sch ssler S.Raw material concepts for SiO2 free high strength castables in the temperature range up to 1200 ℃[A].Aachen,Germany,2002:151-157. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%