分别采用Al2O3涂层处理法和石墨造粒法改善石墨的润湿性,并将改性处理后的石墨引入到矾土基浇注料中,研究了含改性石墨的矾土基浇注料的性能.结果表明:Al2O3涂层对石墨的改性效果不明显,而石墨造粒的改性效果较好;与未处理鳞片石墨相比,造粒石墨中的石墨以微粒的形式分散于浇注料中,使浇注料的需水量大幅度降低,从而使得试样的结构致密,高温抗折强度较高,抗热震性较好.
参考文献
| [1] | 朱伯铨;管红梅;刘文超 .以表面活性剂改善水对鳞片石墨润湿性的研究[J].武汉冶金科技大学学报（自然科学版）,1999,22(03):242-244. |
| [2] | Zhang S;Lee W E.Improving the water-wettability and oxidation resistance of graphite using Al2O3/SiO2 sol-gel coatings[J].Journal of the European Ceramic Society,2003(23):1215-1221. |
| [3] | Ono Y;Matsumoto T;Amemiya Y .Development of the basic monolithic refractories containing hydrophilic graphite[J].Reports Res Lab Asahi Glass Co,Ltd,1993,43(01):35-46. |
| [4] | Koji KAWABATA;Hideyuki YOSHIMATSU;Eiji FUJII .Properties of Al_2O_3-C Castable Refractories with Graphite Powder Coated with Al_2O_3[J].Journal of the Ceramic Society of Japan,2001(1267):270-273. |
| [5] | 王周福,庞业华,孙加林,汪厚植,洪彦若.表面包覆Al（OH）3改性石墨的研究[J].耐火材料,2002(05):266-267,272. |
| [6] | Zhou N S;Rigaud M.Different approaches to incorporating natural flake graphite into Al2O3-SiC-C castables[A].北京,1998:291-297. |
| [7] | 陈加庚 .陶瓷材料抗热震断裂性和抗热震损伤性统一的理论[J].中国陶瓷,1995,31(05):31-34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%