采用热压烧结工艺合成了O'-SialonZrO2-SiC(nm)复合材料,研究了该复合材料的力学性能及显微结构.结果表明,材料抗折强度随温度的变化属Ⅰ类曲线变化规律,Sialon、SiC多晶以及晶粒粗大、层状结构SiC的存在可能是导致材料强度不高的主要原因.断口的显微结构研究表明,复合材料在室温时的断裂以穿晶断裂为主,中、高温时则为沿晶断裂.
参考文献
| [1] | Izaki K;Hakkei K.Ultrastucture processing for advanced ceramics[M].New York: John Willey & Sons,1988:891. |
| [2] | Zhao J;Sterns L C;Harmer M P .Mechanical behavior of alumina - silicon carbide nanocomposites[J].Journal of the American Ceramic Society,1993,76(02):503-510. |
| [3] | 焦绥隆;Borsa C E.氧化铝/碳化硅纳米复合陶瓷的力学性能和强化机理[J].材料导报,1996(z1):89-93. |
| [4] | Niihara K;Hirano T .Nanostructure and thermomechanical of Si3 N4/ SiC composites fabricated from Si - C - N precursor powders[J].Journal of the Japan Society of Powder and Powder Metallurgy,1989,35:243-247. |
| [5] | Nakahira A;Niihara K .The Al2 O3/Si3 N4 nanocomposites[J].粉体おょび粉末冶金(日本),1989,36(02):239-242. |
| [6] | Niihara K;Hirano T;Nakahira A .The Al2O3-SiC-ZrO2 compos-ites[J].粉体おょび粉末冶金(日本),1989,36(06):746-751. |
| [7] | 高家化;沈志坚;丁之上 .陶瓷基纳米复合材料[J].复合材料学报,1994,11(01):1-7. |
| [8] | Hampshire S;Jack K H .Special ceramics 7. Ed. by Taylor D and Popper P[Z].Proc Brit Ceram Soc,1981. |
| [9] | 陈源;黄莉萍;孙兴伟 等.烧结助剂对氮化硅陶瓷高温性能的影响[J].硅酸盐学报,1997,25(02):183-187. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%