利用失重和XRD分析研究了试样组成、合成温度、保温时间和N2分压等工艺条件对粘土碳热还原氮化合成β'-Sialon粉体的影响.结果表明:加入超过化学计量10%的碳,适当提高合成温度和延长保温时间,适当减小氮气分压,都有利于β'-Sialon的形成.轻烧粘土对氮化反应影响不大;β'-Sialon形成过程的分析表明碳热还原氮化反应主要受中间产物CO和SiO的控制.
参考文献
| [1] | 张海军,李文超,钟香崇.粘土还原氮化合成O'-Sialon基复合材料[J].耐火材料,2000(03):137-140. |
| [2] | Lee J G;Cutler I B .Sinterable sialon powder by reaction of clay with carbon and nitrogen[J].American Ceramic Society Bulletin,1979,58(09):869-871. |
| [3] | Baldo J B;Pandolfelli V C;Casarini J R.Relevant parameters in the production of β' -Sialon from natural raw materials via carbothermic reduction[J].Ceramic powders Edited by Vincenzini P Elsevier Amsterdam,1983:437-444. |
| [4] | Higgins I;Hendry A .Production of ββ'-Sialon by carbothermal reduction of kaolinite[J].British Ceramic Transactions,1986,85:161-166. |
| [5] | Van Dijen F K;Metselaar R .Reaction - rate - limiting steps in carbothermal reduction processes[J].Journal of American Cream Soc,1985,68(01):16-19. |
| [6] | 黄莉萍 等.以高岭土制备β—Sialon粉料[J].硅酸盐学报,1991,19(01):11-18. |
| [7] | 张宏泉,戴英,李哗.碳热还原氮化高岭土合成Sialon粉末[J].中国有色金属学报,1998(01):140-144. |
| [8] | 孙俊民 等.以煤矸石为原料制取赛隆陶瓷[J].煤炭加工与综合利用,1998,17(04):17-19. |
| [9] | 陆荚亚 .碳化硅耐火材料中赛隆的工业生产[J].国外耐火材料,1990,15(04):14-20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%