利用自蔓延高温合成技术(self-propagating high temperature syntheris,SHS)合成La0.67Sr0.33MnO3粉体,探讨了自蔓延合成工艺对粉体结构及放电等离子体(spark plasma sintering,SPS)和普通烧结对La0.67Sr0.33MnO3粉体烧结性能和陶瓷显微结构的影响.经XRD,SEM,密度测试等结果表明:在自蔓延法合成出的物相为单一的钙钛矿型结构.SPS烧结与传统的固相烧结法相比:SPS快速烧结大大降低了传统固相法烧结温度,烧结后的晶粒大小基本均匀,烧结体致密度高.经过巨磁电子效应(colossal magnetoresistance,CMR)的测量得出,采用SPS放电等离子烧结的样品相对于普通烧结的样品,低温CMR效应有所增大.
参考文献
[1] | Helmolt R V;Wecker J;Holzapfei B et al.Giant negative magnetoresistance in perovskitelike La1/3 Ba1/3 MnO ferromagnetic films[J].Physical Review Letters,1993,71:2331-2333. |
[2] | Tokura Y.;Kuwahara H.;Asamitsu A.;Moritomo Y.;Kasai M.;Tomioka Y. .ORIGINS OF COLOSSAL MAGNETORESISTANCE IN PEROVSKITE-TYPE MANGANESE OXIDES[J].Journal of Applied Physics,1996(8 Pt.2a):5288-5291. |
[3] | Zhang Ning .Giant magnetoresistance in granular perovskite La0.8Sr0.2MnO3[J].Chinese Physics Letters,1997,14(03):229-232. |
[4] | Wang H;Cheong S W .Enhancing the low field magnetoresistant response in perovskite manganites[J].Applied Physics Letters,1996,68:3494-3496. |
[5] | Palstra T T .Pressure effects on the magnetoresistance in doped manganeses perovskite[J].Physical Review B,1995,52(21):52-55. |
[6] | Gor'kov LP;Kresin VZ .Mixed-valence manganites: fundamentals and main properties[J].Physics Reports: A Review Section of Physics Letters (Section C),2004(3):149-208. |
[7] | Bowen C R;Derby B .Self-propagating high temperature synthesis of ceramic materials[J].British Ceramic Transactions,1997,96(01):25-28. |
[8] | S.W.Wang;L.D.Chen .Densification of Al_2O_3 powder using spark plasma sintering[J].Journal of Materials Research,2000(4):982-987. |
[9] | Hwang H;Cheong S W;Ong O P et al.Spin-polarized intergrain tunneling in La0.7Sr0.3MnO3[J].Physical Review Letters,1996,77:2041-2043. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%